ASTM A959 S32050 vs ASTM A276/A276M N08367

Close Alternative — 73.7% match based on chemical composition and mechanical property overlap.

ASTM A959 S32050 (ASTM A959:2011) and ASTM A276/A276M N08367 (ASTM A276/A276M:2017) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S32050 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A276/A276M N08367 is commonly used for stainless steel bars and shapes (hot-finished or cold-finished). ASTM A959 S32050 is defined under ASTM International, originating from United States, while ASTM A276/A276M N08367 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 S32050 vs ASTM A276/A276M N08367 is a 73.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 73.7%.

Frequently Compared With ASTM A959 S32050:
ASTM A959 2304 ASTM A959 2507 EN 10088-1 1.4401 EN 10088-1 1.4301 ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoH GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
73.7%
MECHANICAL MATCH
No shared data
OVERALL
73.7%
Specifications
Property ASTM A959 S32050 ASTM A276/A276M N08367
Standard ASTM A959:2011 ASTM A276/A276M:2017
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Cr (%) 22.0-24.0 20.0-22.0
Cu (%) <=0.40 <=0.75
Mn (%) <=1.50 <=2.00
Mo (%) 6.0-6.8 6.0-7.0
N (%) 0.21-0.32 0.18-0.25
Ni (%) 20.0-23.0 23.5-25.5
P (%) <=0.035 <=0.040
S (%) <=0.020 <=0.030
Si (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S32050 ASTM A276/A276M N08367
Tensile Strength Not specified >=655 MPa
Yield Strength Not specified >=310 MPa
Elongation Not specified >=30%
Condition Not specified Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)
Typical Applications
ASTM A959 S32050
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A276/A276M N08367
Stainless steel bars and shapes (hot-finished or cold-finished)
Can ASTM A959 S32050 Be Substituted With ASTM A276/A276M N08367?
ASTM A959 S32050 and ASTM A276/A276M N08367 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A959 S32050
0 active listings and RFQs →
ASTM A276/A276M N08367
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S32050 and ASTM A276/A276M N08367?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 S32050 be substituted with ASTM A276/A276M N08367?
ASTM A959 S32050 and ASTM A276/A276M N08367 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.