ASTM A959 S32050 vs ASTM A959 N08367

Close Alternative — 73.7% match based on chemical composition and mechanical property overlap.

ASTM A959 S32050 (ASTM A959:2011) and ASTM A959 N08367 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S32050 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A959 N08367 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A959 S32050 is defined under ASTM International, originating from United States, while ASTM A959 N08367 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 S32050 vs ASTM A959 N08367 is a 73.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 73.7%.

Frequently Compared With ASTM A959 S32050:
ASTM A959 2304 ASTM A959 2507 EN 10088-1 1.4401 EN 10088-1 1.4301 ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoH GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
73.7%
MECHANICAL MATCH
No shared data
OVERALL
73.7%
Specifications
Property ASTM A959 S32050 ASTM A959 N08367
Standard ASTM A959:2011 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Cr (%) 22.0-24.0 20.0-22.0
Cu (%) <=0.40 <=0.75
Mn (%) <=1.50 <=2.00
Mo (%) 6.0-6.8 6.0-7.0
N (%) 0.21-0.32 0.18-0.25
Ni (%) 20.0-23.0 23.5-25.5
P (%) <=0.035 <=0.040
S (%) <=0.020 <=0.030
Si (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Typical Applications
ASTM A959 S32050
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A959 N08367
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can ASTM A959 S32050 Be Substituted With ASTM A959 N08367?
ASTM A959 S32050 and ASTM A959 N08367 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A959 S32050
0 active listings and RFQs →
ASTM A959 N08367
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S32050 and ASTM A959 N08367?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 S32050 be substituted with ASTM A959 N08367?
ASTM A959 S32050 and ASTM A959 N08367 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.