ASTM A959 S32050 vs JIS G4304 SUS836L

Close Alternative — 71.4% match based on chemical composition and mechanical property overlap.

ASTM A959 S32050 (ASTM A959:2011) and JIS G4304 SUS836L (JIS G4304:2021) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S32050 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while JIS G4304 SUS836L is commonly used for hot-rolled stainless steel plates and strips. ASTM A959 S32050 is defined under ASTM International, originating from United States, while JIS G4304 SUS836L is defined under Japanese Industrial Standards (JIS), originating from Japan.

As per chemical composition, ASTM A959 S32050 vs JIS G4304 SUS836L is a 71.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 71.4%.

Frequently Compared With ASTM A959 S32050:
ASTM A959 2304 ASTM A959 2507 EN 10088-1 1.4401 EN 10088-1 1.4301 ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoH GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
71.4%
MECHANICAL MATCH
No shared data
OVERALL
71.4%
Specifications
Property ASTM A959 S32050 JIS G4304 SUS836L
Standard ASTM A959:2011 JIS G4304:2021
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Cr (%) 22.0-24.0 19.00-24.00
Cu (%) <=0.40 Not specified
Mn (%) <=1.50 <=2.00
Mo (%) 6.0-6.8 5.00-7.00
N (%) 0.21-0.32 <=0.25
Ni (%) 20.0-23.0 24.00-26.00
P (%) <=0.035 <=0.045
S (%) <=0.020 <=0.030
Si (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S32050 JIS G4304 SUS836L
Tensile Strength Not specified >=640 MPa
Yield Strength Not specified >=275 MPa
Elongation Not specified >=40%
Hardness Not specified <=217 HB
Condition Not specified Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser
Typical Applications
ASTM A959 S32050
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
JIS G4304 SUS836L
Hot-rolled stainless steel plates and strips
Key Differences
Can ASTM A959 S32050 Be Substituted With JIS G4304 SUS836L?
ASTM A959 S32050 and JIS G4304 SUS836L are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A959 S32050
0 active listings and RFQs →
JIS G4304 SUS836L
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S32050 and JIS G4304 SUS836L?
ASTM A959 S32050 specifies Cu which is not specified for JIS G4304 SUS836L.
Can ASTM A959 S32050 be substituted with JIS G4304 SUS836L?
ASTM A959 S32050 and JIS G4304 SUS836L are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.