ASTM A959 S32053 vs EN 10088-3 X1CrNiMoCuN25-25-5

Close Alternative — 73% match based on chemical composition and mechanical property overlap.

ASTM A959 S32053 (ASTM A959:2011) and EN 10088-3 X1CrNiMoCuN25-25-5 (EN 10088-3:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S32053 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while EN 10088-3 X1CrNiMoCuN25-25-5 is commonly used for general purposes, semi-finished products, bars, rods, wire, sections and bright products. ASTM A959 S32053 is defined under ASTM International, originating from United States, while EN 10088-3 X1CrNiMoCuN25-25-5 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A959 S32053 vs EN 10088-3 X1CrNiMoCuN25-25-5 is a 73% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 73%.

Frequently Compared With ASTM A959 S32053:
ASTM A959 2205 EN 10088-1 1.4006 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoH ASTM A959 .- GB/T 3280 06Cr19Ni10 EN 10088-1 1.4401
Match Breakdown
CHEMISTRY MATCH
73%
MECHANICAL MATCH
No shared data
OVERALL
73%
Specifications
Property ASTM A959 S32053 EN 10088-3 X1CrNiMoCuN25-25-5
Standard ASTM A959:2011 EN 10088-3:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.020
Cr (%) 22.0-24.0 24.0-26.0
Mn (%) <=1.00 <=2.00
Mo (%) 5.0-6.0 4.7-5.7
N (%) 0.17-0.22 0.17-0.25
Ni (%) 24.0-26.0 24.0-27.0
P (%) <=0.030 <=0.030
S (%) <=0.010 <=0.010
Si (%) <=1.00 <=0.70
Cu (%) Not specified 1.00-2.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S32053 EN 10088-3 X1CrNiMoCuN25-25-5
Tensile Strength Not specified 600-800 MPa
Yield Strength Not specified >=300 MPa
Elongation Not specified >=35%
Hardness Not specified <=250 HB
Condition Not specified Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Typical Applications
ASTM A959 S32053
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
EN 10088-3 X1CrNiMoCuN25-25-5
General purposes, semi-finished products, bars, rods, wire, sections and bright products
Key Differences
Can ASTM A959 S32053 Be Substituted With EN 10088-3 X1CrNiMoCuN25-25-5?
ASTM A959 S32053 and EN 10088-3 X1CrNiMoCuN25-25-5 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A959 S32053
0 active listings and RFQs →
EN 10088-3 X1CrNiMoCuN25-25-5
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S32053 and EN 10088-3 X1CrNiMoCuN25-25-5?
EN 10088-3 X1CrNiMoCuN25-25-5 specifies Cu which is not specified for ASTM A959 S32053.
Can ASTM A959 S32053 be substituted with EN 10088-3 X1CrNiMoCuN25-25-5?
ASTM A959 S32053 and EN 10088-3 X1CrNiMoCuN25-25-5 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.