ASTM A959 S32506 vs JIS G4304 SUS329J4L

Close Alternative — 82.7% match based on chemical composition and mechanical property overlap.

ASTM A959 S32506 (ASTM A959:2011) and JIS G4304 SUS329J4L (JIS G4304:2021) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S32506 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while JIS G4304 SUS329J4L is commonly used for hot-rolled stainless steel plates and strips. ASTM A959 S32506 is defined under ASTM International, originating from United States, while JIS G4304 SUS329J4L is defined under Japanese Industrial Standards (JIS), originating from Japan.

As per chemical composition, ASTM A959 S32506 vs JIS G4304 SUS329J4L is a 82.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 82.7%.

Frequently Compared With ASTM A959 S32506:
ASTM A959 2507 ASTM A959 2205 GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12MoVH GOST 5632 08X18H10 EN 10088-1 1.4401 EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
82.7%
MECHANICAL MATCH
No shared data
OVERALL
82.7%
Specifications
Property ASTM A959 S32506 JIS G4304 SUS329J4L
Standard ASTM A959:2011 JIS G4304:2021
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Cr (%) 24.0-26.0 24.00-26.00
Mn (%) <=1.00 <=1.50
Mo (%) 3.0-3.5 2.50-3.50
N (%) 0.08-0.20 0.08-0.30
Ni (%) 5.5-7.2 5.50-7.50
P (%) <=0.040 <=0.040
S (%) <=0.015 <=0.030
Si (%) <=0.90 <=1.00
W (%) 0.05-0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S32506 JIS G4304 SUS329J4L
Tensile Strength Not specified >=620 MPa
Yield Strength Not specified >=450 MPa
Elongation Not specified >=18%
Hardness Not specified <=302 HB
Condition Not specified Solution heat treated plate and strip; proof strength applies only when specified by the purchaser
Typical Applications
ASTM A959 S32506
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
JIS G4304 SUS329J4L
Hot-rolled stainless steel plates and strips
Key Differences
Can ASTM A959 S32506 Be Substituted With JIS G4304 SUS329J4L?
ASTM A959 S32506 and JIS G4304 SUS329J4L are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A959 S32506
0 active listings and RFQs →
JIS G4304 SUS329J4L
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S32506 and JIS G4304 SUS329J4L?
ASTM A959 S32506 specifies W which is not specified for JIS G4304 SUS329J4L.
Can ASTM A959 S32506 be substituted with JIS G4304 SUS329J4L?
ASTM A959 S32506 and JIS G4304 SUS329J4L are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.