Close Alternative — 73% match
based on chemical composition and mechanical property overlap.
ASTM A959 S32950 (ASTM A959:2011) and EN 10088-3 X3CrNiMoN27-5-2 (EN 10088-3:2014) are both steel grades.
Both fall under the Stainless Steel category.
ASTM A959 S32950 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while EN 10088-3 X3CrNiMoN27-5-2 is commonly used for general purposes, semi-finished products, bars, rods, wire, sections and bright products.
ASTM A959 S32950 is defined under ASTM International, originating from United States, while EN 10088-3 X3CrNiMoN27-5-2 is defined under European Standard (EN), originating from Europe.
As per chemical composition, ASTM A959 S32950 vs EN 10088-3 X3CrNiMoN27-5-2 is a 73% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a close alternative overall at 73%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
ASTM A959 S32950
EN 10088-3 X3CrNiMoN27-5-2
Tensile Strength
Not specified
620-880 MPa
Yield Strength
Not specified
>=450 MPa
Elongation
Not specified
>=20%
Hardness
Not specified
<=260 HB
Condition
Not specified
Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Typical Applications
ASTM A959 S32950
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
EN 10088-3 X3CrNiMoN27-5-2
General purposes, semi-finished products, bars, rods, wire, sections and bright products
Can ASTM A959 S32950 Be Substituted With EN 10088-3 X3CrNiMoN27-5-2?
ASTM A959 S32950 and EN 10088-3 X3CrNiMoN27-5-2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between ASTM A959 S32950 and EN 10088-3 X3CrNiMoN27-5-2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 S32950 be substituted with EN 10088-3 X3CrNiMoN27-5-2?
ASTM A959 S32950 and EN 10088-3 X3CrNiMoN27-5-2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.