ASTM A959 S34751 vs IS 1570 (Part 5) X02Cr19Ni10

Close Alternative — 82.6% match based on chemical composition and mechanical property overlap.

ASTM A959 S34751 (ASTM A959:2011) and IS 1570 (Part 5) X02Cr19Ni10 (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S34751 is defined under ASTM International, originating from United States, while IS 1570 (Part 5) X02Cr19Ni10 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 S34751 vs IS 1570 (Part 5) X02Cr19Ni10 is a 82.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 82.6%.

Frequently Compared With ASTM A959 S34751:
EN 10088-1 1.4401 GOST 5632 06Kh23N28 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
82.6%
MECHANICAL MATCH
No shared data
OVERALL
82.6%
Specifications
Property ASTM A959 S34751 IS 1570 (Part 5) X02Cr19Ni10
Standard ASTM A959:2011 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) <=0.015 <=0.030
Cb (%) 0.20-0.50 Not specified
Cr (%) 17.0-20.0 17.5-20.0
Mn (%) <=2.00 <=2.0
N (%) 0.06-0.10 Not specified
Ni (%) 9.0-13.0 8.0-12.0
P (%) <=0.020 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=0.75 <=1.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S34751 IS 1570 (Part 5) X02Cr19Ni10
Tensile Strength Not specified >=485 MPa
Yield Strength Not specified >=170 MPa (0.2 % proof stress)
Elongation Not specified >=40% (50 mm)
Hardness Not specified <=183 HB; <=88 HRB
Condition Not specified Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Typical Applications
ASTM A959 S34751
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 1570 (Part 5) X02Cr19Ni10
Not documented
Key Differences
Can ASTM A959 S34751 Be Substituted With IS 1570 (Part 5) X02Cr19Ni10?
ASTM A959 S34751 and IS 1570 (Part 5) X02Cr19Ni10 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A959 S34751
0 active listings and RFQs →
IS 1570 (Part 5) X02Cr19Ni10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S34751 and IS 1570 (Part 5) X02Cr19Ni10?
ASTM A959 S34751 specifies Cb, N which are not specified for IS 1570 (Part 5) X02Cr19Ni10.
Can ASTM A959 S34751 be substituted with IS 1570 (Part 5) X02Cr19Ni10?
ASTM A959 S34751 and IS 1570 (Part 5) X02Cr19Ni10 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.