ASTM A959 S39274 vs ASTM A276/A276M S32750

Close Alternative — 84.7% match based on chemical composition and mechanical property overlap.

ASTM A959 S39274 (ASTM A959:2011) and ASTM A276/A276M S32750 (ASTM A276/A276M:2017) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S39274 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A276/A276M S32750 is commonly used for stainless steel bars and shapes (hot-finished or cold-finished). ASTM A959 S39274 is defined under ASTM International, originating from United States, while ASTM A276/A276M S32750 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 S39274 vs ASTM A276/A276M S32750 is a 84.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 84.7%.

Frequently Compared With ASTM A959 S39274:
ASTM A959 2507 ASTM A959 .- GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 EN 10088-1 1.4845 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
84.7%
MECHANICAL MATCH
No shared data
OVERALL
84.7%
Specifications
Property ASTM A959 S39274 ASTM A276/A276M S32750
Standard ASTM A959:2011 ASTM A276/A276M:2017
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Cr (%) 24.0-26.0 24.0-26.0
Cu (%) 0.20-0.80 <=0.50
Mn (%) <=1.00 <=1.20
Mo (%) 2.5-3.5 3.0-5.0
N (%) 0.24-0.32 0.24-0.32
Ni (%) 6.0-8.0 6.0-8.0
P (%) <=0.030 <=0.035
S (%) <=0.020 <=0.020
Si (%) <=0.80 <=0.80
W (%) 1.50-2.50 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S39274 ASTM A276/A276M S32750
Tensile Strength Not specified >=800 MPa
Yield Strength Not specified >=550 MPa
Elongation Not specified >=15%
Hardness Not specified <=310 HB
Condition Not specified Condition A (Annealed), hot-finished or cold-finished, up to 2 [50.8] incl sizes (first row printed)
Typical Applications
ASTM A959 S39274
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A276/A276M S32750
Stainless steel bars and shapes (hot-finished or cold-finished)
Key Differences
Can ASTM A959 S39274 Be Substituted With ASTM A276/A276M S32750?
ASTM A959 S39274 and ASTM A276/A276M S32750 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A959 S39274
0 active listings and RFQs →
ASTM A276/A276M S32750
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S39274 and ASTM A276/A276M S32750?
ASTM A959 S39274 specifies W which is not specified for ASTM A276/A276M S32750.
Can ASTM A959 S39274 be substituted with ASTM A276/A276M S32750?
ASTM A959 S39274 and ASTM A276/A276M S32750 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.