ASTM A959 S40910 vs GOST 5632 06Kh23N28

Related Material — 65% match based on chemical composition and mechanical property overlap.

ASTM A959 S40910 (ASTM A959:2011) and GOST 5632 06Kh23N28 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S40910 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while GOST 5632 06Kh23N28 is commonly used for furnace components, heat exchangers, high temperature applications. ASTM A959 S40910 is defined under ASTM International (United States).

As per chemical composition, ASTM A959 S40910 vs GOST 5632 06Kh23N28 is a 65% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 65%.

Frequently Compared With ASTM A959 S40910:
ASTM A959 .- EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12MoVH GOST 5632 08X18H10 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H EN 10088-1 1.4401
Match Breakdown
CHEMISTRY MATCH
65%
MECHANICAL MATCH
No shared data
OVERALL
65%
Specifications
Property ASTM A959 S40910 GOST 5632 06Kh23N28
Standard ASTM A959:2011 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 ≤0.06
Cb (%) <=0.17 Not specified
Cr (%) 10.5-11.7 22.0–25.0
Mn (%) <=1.00 ≤2.00
N (%) <=0.030 Not specified
Ni (%) <=0.50 26.0–29.0
P (%) <=0.040 Not specified
S (%) <=0.020 Not specified
Si (%) <=1.00 ≤0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S40910 GOST 5632 06Kh23N28
Tensile Strength Not specified ≥510 MPa
Yield Strength Not specified ≥196 MPa
Elongation Not specified ≥35%
Max Service Temp Not specified 1050°C
Typical Applications
ASTM A959 S40910
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
Key Differences
Can ASTM A959 S40910 Be Substituted With GOST 5632 06Kh23N28?
ASTM A959 S40910 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A959 S40910
No active listings currently.
GOST 5632 06Kh23N28
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 3100–3400 mm (122.05–133.86 in)
On M-EX Right Now
ASTM A959 S40910
0 active listings and RFQs →
GOST 5632 06Kh23N28
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S40910 and GOST 5632 06Kh23N28?
ASTM A959 S40910 specifies Cb, N, P, S which are not specified for GOST 5632 06Kh23N28.
Can ASTM A959 S40910 be substituted with GOST 5632 06Kh23N28?
ASTM A959 S40910 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.