ASTM A959 S41005 vs BS 970 (Part 3) 416S41

Close Alternative — 70.9% match based on chemical composition and mechanical property overlap.

ASTM A959 S41005 (ASTM A959:2011) and BS 970 (Part 3) 416S41 (BS 970 (Part 3):1991) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S41005 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while BS 970 (Part 3) 416S41 is commonly used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; martensitic stainless steel (table 17). ASTM A959 S41005 is defined under ASTM International, originating from United States, while BS 970 (Part 3) 416S41 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, ASTM A959 S41005 vs BS 970 (Part 3) 416S41 is a 70.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 70.9%.

Frequently Compared With ASTM A959 S41005:
ASTM A959 .- IS 1570 (Part 7) 12Cr12MoH GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845
Match Breakdown
CHEMISTRY MATCH
70.9%
MECHANICAL MATCH
No shared data
OVERALL
70.9%
Specifications
Property ASTM A959 S41005 BS 970 (Part 3) 416S41
Standard ASTM A959:2011 BS 970 (Part 3):1991
Category Stainless Steel Stainless Steel
Al (%) <=0.025 Not specified
C (%) 0.10-0.15 0.09-0.15
Cb (%) <=0.20 Not specified
Cr (%) 11.5-13.0 11.5-13.5
Cu (%) <=0.15 Not specified
Mn (%) 0.25-0.80 <=1.5
Mo (%) <=0.50 <=0.60
N (%) <=0.08 Not specified
Ni (%) <=0.75 <=1.00
P (%) <=0.018 <=0.060
S (%) <=0.015 <=0.060
Si (%) <=0.50 <=1.0
Sn (%) <=0.05 Not specified
Ti (%) <=0.15 Not specified
W (%) <=0.10 Not specified
Se (%) Not specified 0.15-0.35
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Typical Applications
ASTM A959 S41005
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
BS 970 (Part 3) 416S41
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; martensitic stainless steel (Table 17)
Key Differences
Can ASTM A959 S41005 Be Substituted With BS 970 (Part 3) 416S41?
ASTM A959 S41005 and BS 970 (Part 3) 416S41 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A959 S41005
0 active listings and RFQs →
BS 970 (Part 3) 416S41
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S41005 and BS 970 (Part 3) 416S41?
ASTM A959 S41005 specifies Al, Cb, Cu, N which are not specified for BS 970 (Part 3) 416S41. BS 970 (Part 3) 416S41 specifies Se which is not specified for ASTM A959 S41005.
Can ASTM A959 S41005 be substituted with BS 970 (Part 3) 416S41?
ASTM A959 S41005 and BS 970 (Part 3) 416S41 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.