ASTM A959 S41045 vs JIS G4304 SUS410L

Strong Match — 91.4% match based on chemical composition and mechanical property overlap.

ASTM A959 S41045 (ASTM A959:2011) and JIS G4304 SUS410L (JIS G4304:2021) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S41045 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while JIS G4304 SUS410L is commonly used for hot-rolled stainless steel plates and strips. ASTM A959 S41045 is defined under ASTM International, originating from United States, while JIS G4304 SUS410L is defined under Japanese Industrial Standards (JIS), originating from Japan.

As per chemical composition, ASTM A959 S41045 vs JIS G4304 SUS410L is a 91.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 91.4%.

Frequently Compared With ASTM A959 S41045:
ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoVH EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
91.4%
MECHANICAL MATCH
No shared data
OVERALL
91.4%
Specifications
Property ASTM A959 S41045 JIS G4304 SUS410L
Standard ASTM A959:2011 JIS G4304:2021
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Cr (%) 12.0-13.0 11.00-13.50
Mn (%) <=1.00 <=1.00
N (%) <=0.030 Not specified
Ni (%) <=0.50 <=0.60
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S41045 JIS G4304 SUS410L
Tensile Strength Not specified >=360 MPa
Yield Strength Not specified >=195 MPa
Elongation Not specified >=22%
Hardness Not specified <=183 HB
Condition Not specified Annealed plate and strip; proof strength applies only when specified by the purchaser
Typical Applications
ASTM A959 S41045
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
JIS G4304 SUS410L
Hot-rolled stainless steel plates and strips
Key Differences
Can ASTM A959 S41045 Be Substituted With JIS G4304 SUS410L?
ASTM A959 S41045 and JIS G4304 SUS410L overlap closely enough on chemistry and mechanical properties that JIS G4304 SUS410L is often considered as a substitute for ASTM A959 S41045 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 S41045
0 active listings and RFQs →
JIS G4304 SUS410L
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S41045 and JIS G4304 SUS410L?
ASTM A959 S41045 specifies N which is not specified for JIS G4304 SUS410L.
Can ASTM A959 S41045 be substituted with JIS G4304 SUS410L?
ASTM A959 S41045 and JIS G4304 SUS410L overlap closely enough on chemistry and mechanical properties that JIS G4304 SUS410L is often considered as a substitute for ASTM A959 S41045 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.