ASTM A959 S41425 vs IS 6603 X03Cr27Ni5Mo2N

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

ASTM A959 S41425 (ASTM A959:2011) and IS 6603 X03Cr27Ni5Mo2N (IS 6603:2024) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S41425 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 6603 X03Cr27Ni5Mo2N is commonly used for general purposes, semi-finished products, bars, wire rods and bright bars. ASTM A959 S41425 is defined under ASTM International, originating from United States, while IS 6603 X03Cr27Ni5Mo2N is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 S41425 vs IS 6603 X03Cr27Ni5Mo2N is a 70.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With ASTM A959 S41425:
IS 1570 (Part 7) 11Cr17Ni13W3TiH EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 ASTM A959 255
Match Breakdown
CHEMISTRY MATCH
70.9%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property ASTM A959 S41425 IS 6603 X03Cr27Ni5Mo2N
Standard ASTM A959:2011 IS 6603:2024
Category Stainless Steel Stainless Steel
C (%) <=0.05 <=0.050
Cr (%) 12.0-15.0 25.0-28.0
Cu (%) <=0.30 Not specified
Mn (%) 0.50-1.00 <=2.00
Mo (%) 1.50-2.00 1.30-2.00
N (%) 0.06-0.12 0.05-0.20
Ni (%) 4.0-7.0 4.5-6.5
P (%) <=0.020 <=0.035
S (%) <=0.005 <=0.015
Si (%) <=0.50 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S41425 IS 6603 X03Cr27Ni5Mo2N
Tensile Strength Not specified >=620 MPa
Yield Strength Not specified >=450 MPa
Elongation Not specified >=20%
Hardness Not specified <=260 HB
Condition Not specified Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Tensile Strength is a minimum as printed, hardness for guidance only
Typical Applications
ASTM A959 S41425
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 6603 X03Cr27Ni5Mo2N
General purposes, semi-finished products, bars, wire rods and bright bars
Key Differences
Can ASTM A959 S41425 Be Substituted With IS 6603 X03Cr27Ni5Mo2N?
ASTM A959 S41425 and IS 6603 X03Cr27Ni5Mo2N share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A959 S41425
0 active listings and RFQs →
IS 6603 X03Cr27Ni5Mo2N
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S41425 and IS 6603 X03Cr27Ni5Mo2N?
ASTM A959 S41425 specifies Cu which is not specified for IS 6603 X03Cr27Ni5Mo2N.
Can ASTM A959 S41425 be substituted with IS 6603 X03Cr27Ni5Mo2N?
ASTM A959 S41425 and IS 6603 X03Cr27Ni5Mo2N share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.