ASTM A959 S41500 vs ASTM A276/A276M S41500

Strong Match — 100% match based on chemical composition and mechanical property overlap.

ASTM A959 S41500 (ASTM A959:2011) and ASTM A276/A276M S41500 (ASTM A276/A276M:2017) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S41500 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A276/A276M S41500 is commonly used for stainless steel bars and shapes (hot-finished or cold-finished). ASTM A959 S41500 is defined under ASTM International, originating from United States, while ASTM A276/A276M S41500 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 S41500 vs ASTM A276/A276M S41500 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With ASTM A959 S41500:
EN 10088-1 1.4006 ASTM A959 25-4-4 EN 10088-1 1.4845 ASTM A959 26-3-3 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoVH GOST 5632 06Kh23N28 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 ASTM A959 29-4C
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property ASTM A959 S41500 ASTM A276/A276M S41500
Standard ASTM A959:2011 ASTM A276/A276M:2017
Category Stainless Steel Stainless Steel
C (%) <=0.05 <=0.05
Cr (%) 11.5-14.0 11.5-14.0
Mn (%) 0.50-1.00 0.50-1.00
Mo (%) 0.50-1.00 0.50-1.00
Ni (%) 3.5-5.5 3.5-5.5
P (%) <=0.030 <=0.030
S (%) <=0.030 <=0.030
Si (%) <=0.60 <=0.60
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S41500 ASTM A276/A276M S41500
Tensile Strength Not specified >=795 MPa
Yield Strength Not specified >=620 MPa
Elongation Not specified >=15%
Hardness Not specified <=295 HB
Condition Not specified Condition T (Hardened and tempered, higher temperature), hot-finished or cold-finished, all sizes (first row printed)
Typical Applications
ASTM A959 S41500
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A276/A276M S41500
Stainless steel bars and shapes (hot-finished or cold-finished)
Can ASTM A959 S41500 Be Substituted With ASTM A276/A276M S41500?
ASTM A959 S41500 and ASTM A276/A276M S41500 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S41500 is often considered as a substitute for ASTM A959 S41500 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 S41500
0 active listings and RFQs →
ASTM A276/A276M S41500
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S41500 and ASTM A276/A276M S41500?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 S41500 be substituted with ASTM A276/A276M S41500?
ASTM A959 S41500 and ASTM A276/A276M S41500 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S41500 is often considered as a substitute for ASTM A959 S41500 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.