ASTM A959 S41500 vs EN 10088-2 X3CrNiMo13-4

Close Alternative — 76.1% match based on chemical composition and mechanical property overlap.

ASTM A959 S41500 (ASTM A959:2011) and EN 10088-2 X3CrNiMo13-4 (EN 10088-2:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S41500 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while EN 10088-2 X3CrNiMo13-4 is commonly used for general purposes, hot or cold rolled sheet/plate and strip. ASTM A959 S41500 is defined under ASTM International, originating from United States, while EN 10088-2 X3CrNiMo13-4 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A959 S41500 vs EN 10088-2 X3CrNiMo13-4 is a 76.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 76.1%.

Frequently Compared With ASTM A959 S41500:
EN 10088-1 1.4006 ASTM A959 25-4-4 EN 10088-1 1.4845 ASTM A959 26-3-3 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoVH GOST 5632 06Kh23N28 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 ASTM A959 29-4C
Match Breakdown
CHEMISTRY MATCH
76.1%
MECHANICAL MATCH
No shared data
OVERALL
76.1%
Specifications
Property ASTM A959 S41500 EN 10088-2 X3CrNiMo13-4
Standard ASTM A959:2011 EN 10088-2:2014
Category Stainless Steel Stainless Steel
C (%) <=0.05 <=0.05
Cr (%) 11.5-14.0 12.0-14.0
Mn (%) 0.50-1.00 <=1.50
Mo (%) 0.50-1.00 0.30-0.70
Ni (%) 3.5-5.5 3.5-4.5
P (%) <=0.030 <=0.040
S (%) <=0.030 <=0.015
Si (%) <=0.60 <=0.70
N (%) Not specified >=0.020
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S41500 EN 10088-2 X3CrNiMo13-4
Tensile Strength Not specified 780-980 MPa
Yield Strength Not specified >=630 MPa
Elongation Not specified >=15%
Condition Not specified Quenched and tempered (+QT780), hot rolled plate, up to 75 mm thick
Typical Applications
ASTM A959 S41500
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
EN 10088-2 X3CrNiMo13-4
General purposes, hot or cold rolled sheet/plate and strip
Key Differences
Can ASTM A959 S41500 Be Substituted With EN 10088-2 X3CrNiMo13-4?
ASTM A959 S41500 and EN 10088-2 X3CrNiMo13-4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A959 S41500
0 active listings and RFQs →
EN 10088-2 X3CrNiMo13-4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S41500 and EN 10088-2 X3CrNiMo13-4?
EN 10088-2 X3CrNiMo13-4 specifies N which is not specified for ASTM A959 S41500.
Can ASTM A959 S41500 be substituted with EN 10088-2 X3CrNiMo13-4?
ASTM A959 S41500 and EN 10088-2 X3CrNiMo13-4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.