ASTM A959 S43932 vs JIS G4304 SUS430LX

Close Alternative — 84.8% match based on chemical composition and mechanical property overlap.

ASTM A959 S43932 (ASTM A959:2011) and JIS G4304 SUS430LX (JIS G4304:2021) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S43932 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while JIS G4304 SUS430LX is commonly used for hot-rolled stainless steel plates and strips. ASTM A959 S43932 is defined under ASTM International, originating from United States, while JIS G4304 SUS430LX is defined under Japanese Industrial Standards (JIS), originating from Japan.

As per chemical composition, ASTM A959 S43932 vs JIS G4304 SUS430LX is a 84.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 84.8%.

Frequently Compared With ASTM A959 S43932:
ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
84.8%
MECHANICAL MATCH
No shared data
OVERALL
84.8%
Specifications
Property ASTM A959 S43932 JIS G4304 SUS430LX
Standard ASTM A959:2011 JIS G4304:2021
Category Stainless Steel Stainless Steel
Al (%) <=0.15 Not specified
C (%) <=0.030 <=0.030
Cr (%) 17.0-19.0 16.00-19.00
Mn (%) <=1.00 <=1.00
N (%) <=0.030 Not specified
Ni (%) <=0.50 <=0.60
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=0.75
Ti (%) Not specified 0.10-1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S43932 JIS G4304 SUS430LX
Tensile Strength Not specified >=360 MPa
Yield Strength Not specified >=175 MPa
Elongation Not specified >=22%
Hardness Not specified <=183 HB
Condition Not specified Annealed plate and strip; proof strength applies only when specified by the purchaser
Typical Applications
ASTM A959 S43932
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
JIS G4304 SUS430LX
Hot-rolled stainless steel plates and strips
Key Differences
Can ASTM A959 S43932 Be Substituted With JIS G4304 SUS430LX?
ASTM A959 S43932 and JIS G4304 SUS430LX are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A959 S43932
0 active listings and RFQs →
JIS G4304 SUS430LX
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S43932 and JIS G4304 SUS430LX?
ASTM A959 S43932 specifies Al, N which are not specified for JIS G4304 SUS430LX. JIS G4304 SUS430LX specifies Ti which is not specified for ASTM A959 S43932.
Can ASTM A959 S43932 be substituted with JIS G4304 SUS430LX?
ASTM A959 S43932 and JIS G4304 SUS430LX are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.