ASTM A959 S44500 vs ASTM A240/A240M S43932

Close Alternative — 81.2% match based on chemical composition and mechanical property overlap.

ASTM A959 S44500 (ASTM A959:2011) and ASTM A240/A240M S43932 (ASTM A240/A240M:2025) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S44500 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A240/A240M S43932 is commonly used for pressure vessels and general applications (plate, sheet and strip). ASTM A959 S44500 is defined under ASTM International, originating from United States, while ASTM A240/A240M S43932 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 S44500 vs ASTM A240/A240M S43932 is a 81.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 81.2%.

Frequently Compared With ASTM A959 S44500:
ASTM A959 .- EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10
Match Breakdown
CHEMISTRY MATCH
81.2%
MECHANICAL MATCH
No shared data
OVERALL
81.2%
Specifications
Property ASTM A959 S44500 ASTM A240/A240M S43932
Standard ASTM A959:2011 ASTM A240/A240M:2025
Category Stainless Steel Stainless Steel
C (%) <=0.020 <=0.030
Cr (%) 19.0-21.0 17.0-19.0
Cu (%) 0.30-0.60 Not specified
Mn (%) <=1.00 <=1.00
N (%) <=0.03 <=0.030
Ni (%) <=0.60 <=0.50
P (%) <=0.040 <=0.040
S (%) <=0.012 <=0.030
Si (%) <=1.00 <=1.00
Al (%) Not specified <=0.15
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S44500 ASTM A240/A240M S43932
Tensile Strength Not specified >=415 MPa
Yield Strength Not specified >=205 MPa
Elongation Not specified >=22%
Hardness Not specified <=183 HB
Condition Not specified Plate, sheet and strip; yield by 0.2 percent offset
Typical Applications
ASTM A959 S44500
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A240/A240M S43932
Pressure vessels and general applications (plate, sheet and strip)
Key Differences
Can ASTM A959 S44500 Be Substituted With ASTM A240/A240M S43932?
ASTM A959 S44500 and ASTM A240/A240M S43932 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A959 S44500
0 active listings and RFQs →
ASTM A240/A240M S43932
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S44500 and ASTM A240/A240M S43932?
ASTM A959 S44500 specifies Cu which is not specified for ASTM A240/A240M S43932. ASTM A240/A240M S43932 specifies Al which is not specified for ASTM A959 S44500.
Can ASTM A959 S44500 be substituted with ASTM A240/A240M S43932?
ASTM A959 S44500 and ASTM A240/A240M S43932 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.