ASTM A959 XM-1 vs IS 1570 (Part 5) X10Cr17Mn6Ni4

Close Alternative — 79% match based on chemical composition and mechanical property overlap.

ASTM A959 XM-1 (ASTM A959:2011) and IS 1570 (Part 5) X10Cr17Mn6Ni4 (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 XM-1 is defined under ASTM International, originating from United States, while IS 1570 (Part 5) X10Cr17Mn6Ni4 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 XM-1 vs IS 1570 (Part 5) X10Cr17Mn6Ni4 is a 79% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 79%.

Frequently Compared With ASTM A959 XM-1:
IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 201 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .- EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 GOST 5632 08X18H10
Match Breakdown
CHEMISTRY MATCH
79%
MECHANICAL MATCH
No shared data
OVERALL
79%
Specifications
Property ASTM A959 XM-1 IS 1570 (Part 5) X10Cr17Mn6Ni4
Standard ASTM A959:2011 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.20
Cr (%) 16.0-18.0 16.0-18.0
Cu (%) 1.75-2.25 Not specified
Mn (%) 5.0-6.5 4.0-8.0
Ni (%) 5.0-6.5 3.5-5.5
P (%) <=0.045 <=0.045
S (%) 0.18-0.35 <=0.030
Si (%) <=1.00 <=1.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 XM-1 IS 1570 (Part 5) X10Cr17Mn6Ni4
Tensile Strength Not specified >=515 MPa
Yield Strength Not specified >=275 MPa (0.2 % proof stress)
Elongation Not specified >=40% (50 mm)
Hardness Not specified <=217 HB
Condition Not specified Annealed, quenched or solution treated bars and flats (Table 3)
Typical Applications
ASTM A959 XM-1
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 1570 (Part 5) X10Cr17Mn6Ni4
Not documented
Key Differences
Can ASTM A959 XM-1 Be Substituted With IS 1570 (Part 5) X10Cr17Mn6Ni4?
ASTM A959 XM-1 and IS 1570 (Part 5) X10Cr17Mn6Ni4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A959 XM-1
0 active listings and RFQs →
IS 1570 (Part 5) X10Cr17Mn6Ni4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 XM-1 and IS 1570 (Part 5) X10Cr17Mn6Ni4?
ASTM A959 XM-1 specifies Cu which is not specified for IS 1570 (Part 5) X10Cr17Mn6Ni4.
Can ASTM A959 XM-1 be substituted with IS 1570 (Part 5) X10Cr17Mn6Ni4?
ASTM A959 XM-1 and IS 1570 (Part 5) X10Cr17Mn6Ni4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.