Close Alternative — 75.1% match
based on chemical composition and mechanical property overlap.
ASTM A959 XM-10 (ASTM A959:2011) and IS 6911 X10Cr18Mn9Ni5 (IS 6911:1992) are both steel grades.
Both fall under the Stainless Steel category.
ASTM A959 XM-10 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 6911 X10Cr18Mn9Ni5 is commonly used for stainless and heat-resisting steel plate, sheet and strip (clause 1.1).
ASTM A959 XM-10 is defined under ASTM International, originating from United States, while IS 6911 X10Cr18Mn9Ni5 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, ASTM A959 XM-10 vs IS 6911 X10Cr18Mn9Ni5 is a 75.1% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a close alternative overall at 75.1%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
ASTM A959 XM-10
IS 6911 X10Cr18Mn9Ni5
Bend Test (180 deg)
Not specified
Not required
Elongation (50 mm, annealed)
Not specified
>=40%
Hardness (annealed, max)
Not specified
217 HBS, 95 HRB
Tensile Strength (annealed)
Not specified
>=620 MPa
Yield Strength (0.2% proof, annealed)
Not specified
>=310 MPa
Typical Applications
ASTM A959 XM-10
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 6911 X10Cr18Mn9Ni5
Stainless and heat-resisting steel plate, sheet and strip (clause 1.1)
Key Differences
ASTM A959 XM-10 specifies N which is not specified for IS 6911 X10Cr18Mn9Ni5.
Can ASTM A959 XM-10 Be Substituted With IS 6911 X10Cr18Mn9Ni5?
ASTM A959 XM-10 and IS 6911 X10Cr18Mn9Ni5 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between ASTM A959 XM-10 and IS 6911 X10Cr18Mn9Ni5?
ASTM A959 XM-10 specifies N which is not specified for IS 6911 X10Cr18Mn9Ni5.
Can ASTM A959 XM-10 be substituted with IS 6911 X10Cr18Mn9Ni5?
ASTM A959 XM-10 and IS 6911 X10Cr18Mn9Ni5 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.