ASTM A959 XM-11 vs IS 11169 (Part 2) X02Cr19Ni11

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

ASTM A959 XM-11 (ASTM A959:2011) and IS 11169 (Part 2) X02Cr19Ni11 (IS 11169 (Part 2):2023) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 XM-11 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 11169 (Part 2) X02Cr19Ni11 is commonly used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11). ASTM A959 XM-11 is defined under ASTM International, originating from United States, while IS 11169 (Part 2) X02Cr19Ni11 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 XM-11 vs IS 11169 (Part 2) X02Cr19Ni11 is a 69.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With ASTM A959 XM-11:
EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH GOST 5632 08X18H10 ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
69.9%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property ASTM A959 XM-11 IS 11169 (Part 2) X02Cr19Ni11
Standard ASTM A959:2011 IS 11169 (Part 2):2023
Category Stainless Steel Stainless Steel
C (%) <=0.04 <=0.030
Cr (%) 19.0-21.5 18.0-20.0
Mn (%) 8.0-10.0 <=2.00
N (%) 0.15-0.40 <=0.10
Ni (%) 5.5-7.5 10.0-12.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Cu (%) Not specified <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 XM-11 IS 11169 (Part 2) X02Cr19Ni11
Reduction of Area, solution annealed (+AT) Not specified >=68% (over 5 to 50 mm)
Tensile Strength, solution annealed (+AT) Not specified <=630 MPa (over 5 to 50 mm)
Typical Applications
ASTM A959 XM-11
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 11169 (Part 2) X02Cr19Ni11
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
Key Differences
Can ASTM A959 XM-11 Be Substituted With IS 11169 (Part 2) X02Cr19Ni11?
ASTM A959 XM-11 and IS 11169 (Part 2) X02Cr19Ni11 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A959 XM-11
0 active listings and RFQs →
IS 11169 (Part 2) X02Cr19Ni11
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 XM-11 and IS 11169 (Part 2) X02Cr19Ni11?
IS 11169 (Part 2) X02Cr19Ni11 specifies Cu which is not specified for ASTM A959 XM-11.
Can ASTM A959 XM-11 be substituted with IS 11169 (Part 2) X02Cr19Ni11?
ASTM A959 XM-11 and IS 11169 (Part 2) X02Cr19Ni11 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.