ASTM A959 XM-13 vs JIS G4303 SUS316

Related Material — 64.6% match based on chemical composition and mechanical property overlap.

ASTM A959 XM-13 (ASTM A959:2011) and JIS G4303 SUS316 (JIS G4303:2021) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 XM-13 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while JIS G4303 SUS316 is commonly used for marine applications, chemical processing, pharmaceutical equipment. ASTM A959 XM-13 is defined under ASTM International, originating from United States, while JIS G4303 SUS316 is defined under Japanese Industrial Standards (JIS), originating from Japan.

As per chemical composition, ASTM A959 XM-13 vs JIS G4303 SUS316 is a 64.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 64.6%.

Frequently Compared With ASTM A959 XM-13:
ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH GB/T 3280 06Cr19Ni10
Match Breakdown
CHEMISTRY MATCH
64.6%
MECHANICAL MATCH
No shared data
OVERALL
64.6%
Specifications
Property ASTM A959 XM-13 JIS G4303 SUS316
Standard ASTM A959:2011 JIS G4303:2021
Category Stainless Steel Stainless Steel
Al (%) 0.90-1.35 Not specified
C (%) <=0.05 ≤0.08
Cr (%) 12.3-13.2 16.0–18.0
Mn (%) <=0.20 ≤2.00
Mo (%) 2.00-3.00 2.0–3.0
N (%) <=0.01 Not specified
Ni (%) 7.5-8.5 10.0–14.0
P (%) <=0.010 Not specified
S (%) <=0.008 Not specified
Si (%) <=0.10 ≤1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 XM-13 JIS G4303 SUS316
Tensile Strength Not specified ≥520 MPa
Yield Strength Not specified ≥205 MPa
Elongation Not specified ≥40%
Hardness Not specified ≤187 HB
Typical Applications
ASTM A959 XM-13
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
JIS G4303 SUS316
Marine applications, chemical processing, pharmaceutical equipment
Key Differences
Can ASTM A959 XM-13 Be Substituted With JIS G4303 SUS316?
ASTM A959 XM-13 and JIS G4303 SUS316 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A959 XM-13
No active listings currently.
JIS G4303 SUS316
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2800–3300 mm (110.24–129.92 in)
On M-EX Right Now
ASTM A959 XM-13
0 active listings and RFQs →
JIS G4303 SUS316
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 XM-13 and JIS G4303 SUS316?
ASTM A959 XM-13 specifies Al, N, P, S which are not specified for JIS G4303 SUS316.
Can ASTM A959 XM-13 be substituted with JIS G4303 SUS316?
ASTM A959 XM-13 and JIS G4303 SUS316 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.