ASTM A959 XM-15 (S38100) vs GB/T 3280 06Cr19Ni10

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

ASTM A959 XM-15 (S38100) (ASTM A959:2011) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 XM-15 (S38100) is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while GB/T 3280 06Cr19Ni10 is commonly used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.. ASTM A959 XM-15 (S38100) is defined under ASTM International, originating from United States, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, ASTM A959 XM-15 (S38100) vs GB/T 3280 06Cr19Ni10 is a 79.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With ASTM A959 XM-15 (S38100):
GOST 5632 08X18H10 ASTM A959 .- IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
79.6%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property ASTM A959 XM-15 (S38100) GB/T 3280 06Cr19Ni10
Standard ASTM A959:2011 GB/T 3280-2015
Category Stainless Steel Stainless Steel
C (%) <=0.08 0.08 max
Cr (%) 17.0-19.0 18.00-20.00
Mn (%) <=2.00 2.00 max
Ni (%) 17.5-18.5 8.00-11.00
P (%) <=0.030 0.045 max
S (%) <=0.030 0.030 max
Si (%) 1.50-2.50 1.00 max
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 XM-15 (S38100) GB/T 3280 06Cr19Ni10
Tensile Strength Not specified 520-720 MPa
Yield Strength Not specified 205-310 MPa
Elongation Not specified 40-60%
Hardness Not specified 187 HB max
Typical Applications
ASTM A959 XM-15 (S38100)
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Can ASTM A959 XM-15 (S38100) Be Substituted With GB/T 3280 06Cr19Ni10?
ASTM A959 XM-15 (S38100) and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A959 XM-15 (S38100)
No active listings currently.
GB/T 3280 06Cr19Ni10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2900–3300 mm (114.17–129.92 in)
On M-EX Right Now
ASTM A959 XM-15 (S38100)
0 active listings and RFQs →
GB/T 3280 06Cr19Ni10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 XM-15 (S38100) and GB/T 3280 06Cr19Ni10?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 XM-15 (S38100) be substituted with GB/T 3280 06Cr19Ni10?
ASTM A959 XM-15 (S38100) and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.