ASTM A959 XM-19 vs ASTM A240/A240M S20910

Strong Match — 92.7% match based on chemical composition and mechanical property overlap.

ASTM A959 XM-19 (ASTM A959:2011) and ASTM A240/A240M S20910 (ASTM A240/A240M:2025) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 XM-19 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A240/A240M S20910 is commonly used for pressure vessels and general applications (plate, sheet and strip). ASTM A959 XM-19 is defined under ASTM International, originating from United States, while ASTM A240/A240M S20910 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 XM-19 vs ASTM A240/A240M S20910 is a 92.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 92.7%.

Frequently Compared With ASTM A959 XM-19:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr13H EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo EN 10088-1 1.4006 EN 10088-1 1.4401
Match Breakdown
CHEMISTRY MATCH
92.7%
MECHANICAL MATCH
No shared data
OVERALL
92.7%
Specifications
Property ASTM A959 XM-19 ASTM A240/A240M S20910
Standard ASTM A959:2011 ASTM A240/A240M:2025
Category Stainless Steel Stainless Steel
C (%) <=0.06 <=0.06
Cb (%) 0.10-0.30 Not specified
Cr (%) 20.5-23.5 20.5-23.5
Mn (%) 4.0-6.0 4.00-6.00
Mo (%) 1.50-3.00 1.50-3.00
N (%) 0.20-0.40 0.20-0.40
Ni (%) 11.5-13.5 11.5-13.5
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=0.75
V (%) 0.10-0.30 0.10-0.30
Nb (%) Not specified 0.10-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 XM-19 ASTM A240/A240M S20910
Tensile Strength Not specified >=725 MPa
Yield Strength Not specified >=415 MPa
Elongation Not specified >=30%
Hardness Not specified <=241 HB
Condition Not specified Sheet and strip (first condition printed); yield by 0.2 percent offset
Typical Applications
ASTM A959 XM-19
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A240/A240M S20910
Pressure vessels and general applications (plate, sheet and strip)
Key Differences
Can ASTM A959 XM-19 Be Substituted With ASTM A240/A240M S20910?
ASTM A959 XM-19 and ASTM A240/A240M S20910 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S20910 is often considered as a substitute for ASTM A959 XM-19 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 XM-19
0 active listings and RFQs →
ASTM A240/A240M S20910
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 XM-19 and ASTM A240/A240M S20910?
ASTM A959 XM-19 specifies Cb which is not specified for ASTM A240/A240M S20910. ASTM A240/A240M S20910 specifies Nb which is not specified for ASTM A959 XM-19.
Can ASTM A959 XM-19 be substituted with ASTM A240/A240M S20910?
ASTM A959 XM-19 and ASTM A240/A240M S20910 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S20910 is often considered as a substitute for ASTM A959 XM-19 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.