ASTM A959 XM-19 vs JIS G4304 SUS316N

Related Material — 66.3% match based on chemical composition and mechanical property overlap.

ASTM A959 XM-19 (ASTM A959:2011) and JIS G4304 SUS316N (JIS G4304:2021) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 XM-19 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while JIS G4304 SUS316N is commonly used for hot-rolled stainless steel plates and strips. ASTM A959 XM-19 is defined under ASTM International, originating from United States, while JIS G4304 SUS316N is defined under Japanese Industrial Standards (JIS), originating from Japan.

As per chemical composition, ASTM A959 XM-19 vs JIS G4304 SUS316N is a 66.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 66.3%.

Frequently Compared With ASTM A959 XM-19:
ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
66.3%
MECHANICAL MATCH
No shared data
OVERALL
66.3%
Specifications
Property ASTM A959 XM-19 JIS G4304 SUS316N
Standard ASTM A959:2011 JIS G4304:2021
Category Stainless Steel Stainless Steel
C (%) <=0.06 <=0.08
Cb (%) 0.10-0.30 Not specified
Cr (%) 20.5-23.5 16.00-18.00
Mn (%) 4.0-6.0 <=2.00
Mo (%) 1.50-3.00 2.00-3.00
N (%) 0.20-0.40 0.10-0.22
Ni (%) 11.5-13.5 10.00-14.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
V (%) 0.10-0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 XM-19 JIS G4304 SUS316N
Tensile Strength Not specified >=550 MPa
Yield Strength Not specified >=275 MPa
Elongation Not specified >=35%
Hardness Not specified <=217 HB
Condition Not specified Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser
Typical Applications
ASTM A959 XM-19
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
JIS G4304 SUS316N
Hot-rolled stainless steel plates and strips
Key Differences
Can ASTM A959 XM-19 Be Substituted With JIS G4304 SUS316N?
ASTM A959 XM-19 and JIS G4304 SUS316N share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A959 XM-19
0 active listings and RFQs →
JIS G4304 SUS316N
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 XM-19 and JIS G4304 SUS316N?
ASTM A959 XM-19 specifies Cb, V which are not specified for JIS G4304 SUS316N.
Can ASTM A959 XM-19 be substituted with JIS G4304 SUS316N?
ASTM A959 XM-19 and JIS G4304 SUS316N share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.