ASTM A959 XM-27 vs ASTM A240/A240M S44725

Close Alternative — 73.8% match based on chemical composition and mechanical property overlap.

ASTM A959 XM-27 (ASTM A959:2011) and ASTM A240/A240M S44725 (ASTM A240/A240M:2025) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 XM-27 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A240/A240M S44725 is commonly used for pressure vessels and general applications (plate, sheet and strip). ASTM A959 XM-27 is defined under ASTM International, originating from United States, while ASTM A240/A240M S44725 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 XM-27 vs ASTM A240/A240M S44725 is a 73.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 73.8%.

Frequently Compared With ASTM A959 XM-27:
ASTM A959 29-4 ASTM A959 29-4-2 IS 1570 (Part 7) 12Cr12MoH GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH ASTM A959 26-3-3 ASTM A959 .- EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
73.8%
MECHANICAL MATCH
No shared data
OVERALL
73.8%
Specifications
Property ASTM A959 XM-27 ASTM A240/A240M S44725
Standard ASTM A959:2011 ASTM A240/A240M:2025
Category Stainless Steel Stainless Steel
C (%) <=0.010 <=0.015
Cb (%) 0.05-0.20 Not specified
Cr (%) 25.0-27.5 25.0-28.5
Cu (%) <=0.20 Not specified
Mn (%) <=0.40 <=0.40
Mo (%) 0.75-1.50 1.5-2.5
N (%) <=0.015 <=0.018
Ni (%) <=0.50 <=0.30
P (%) <=0.020 <=0.040
S (%) <=0.020 <=0.020
Si (%) <=0.40 <=0.040
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 XM-27 ASTM A240/A240M S44725
Tensile Strength Not specified >=450 MPa
Yield Strength Not specified >=275 MPa
Elongation Not specified >=20%
Hardness Not specified <=210 HB
Condition Not specified Plate, sheet and strip; yield by 0.2 percent offset
Typical Applications
ASTM A959 XM-27
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A240/A240M S44725
Pressure vessels and general applications (plate, sheet and strip)
Key Differences
Can ASTM A959 XM-27 Be Substituted With ASTM A240/A240M S44725?
ASTM A959 XM-27 and ASTM A240/A240M S44725 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A959 XM-27
0 active listings and RFQs →
ASTM A240/A240M S44725
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 XM-27 and ASTM A240/A240M S44725?
ASTM A959 XM-27 specifies Cb, Cu which are not specified for ASTM A240/A240M S44725.
Can ASTM A959 XM-27 be substituted with ASTM A240/A240M S44725?
ASTM A959 XM-27 and ASTM A240/A240M S44725 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.