ASTM A959 XM-27 vs JIS G4304 SUSXM27

Strong Match — 99.1% match based on chemical composition and mechanical property overlap.

ASTM A959 XM-27 (ASTM A959:2011) and JIS G4304 SUSXM27 (JIS G4304:2021) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 XM-27 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while JIS G4304 SUSXM27 is commonly used for hot-rolled stainless steel plates and strips. ASTM A959 XM-27 is defined under ASTM International, originating from United States, while JIS G4304 SUSXM27 is defined under Japanese Industrial Standards (JIS), originating from Japan.

As per chemical composition, ASTM A959 XM-27 vs JIS G4304 SUSXM27 is a 99.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 99.1%.

Frequently Compared With ASTM A959 XM-27:
ASTM A959 29-4 ASTM A959 29-4-2 IS 1570 (Part 7) 12Cr12MoH GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH ASTM A959 26-3-3 ASTM A959 .- EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
99.1%
MECHANICAL MATCH
No shared data
OVERALL
99.1%
Specifications
Property ASTM A959 XM-27 JIS G4304 SUSXM27
Standard ASTM A959:2011 JIS G4304:2021
Category Stainless Steel Stainless Steel
C (%) <=0.010 <=0.010
Cb (%) 0.05-0.20 Not specified
Cr (%) 25.0-27.5 25.00-27.50
Cu (%) <=0.20 <=0.20
Mn (%) <=0.40 <=0.40
Mo (%) 0.75-1.50 0.75-1.50
N (%) <=0.015 <=0.015
Ni (%) <=0.50 <=0.50
P (%) <=0.020 <=0.030
S (%) <=0.020 <=0.020
Si (%) <=0.40 <=0.40
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 XM-27 JIS G4304 SUSXM27
Tensile Strength Not specified >=410 MPa
Yield Strength Not specified >=245 MPa
Elongation Not specified >=22%
Hardness Not specified <=192 HB
Condition Not specified Annealed plate and strip; proof strength applies only when specified by the purchaser
Typical Applications
ASTM A959 XM-27
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
JIS G4304 SUSXM27
Hot-rolled stainless steel plates and strips
Key Differences
Can ASTM A959 XM-27 Be Substituted With JIS G4304 SUSXM27?
ASTM A959 XM-27 and JIS G4304 SUSXM27 overlap closely enough on chemistry and mechanical properties that JIS G4304 SUSXM27 is often considered as a substitute for ASTM A959 XM-27 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 XM-27
0 active listings and RFQs →
JIS G4304 SUSXM27
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 XM-27 and JIS G4304 SUSXM27?
ASTM A959 XM-27 specifies Cb which is not specified for JIS G4304 SUSXM27.
Can ASTM A959 XM-27 be substituted with JIS G4304 SUSXM27?
ASTM A959 XM-27 and JIS G4304 SUSXM27 overlap closely enough on chemistry and mechanical properties that JIS G4304 SUSXM27 is often considered as a substitute for ASTM A959 XM-27 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.