ASTM A959 XM-28 vs EN 10088-3 X13MnNiN18-13-2

Strong Match — 100% match based on chemical composition and mechanical property overlap.

ASTM A959 XM-28 (ASTM A959:2011) and EN 10088-3 X13MnNiN18-13-2 (EN 10088-3:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 XM-28 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while EN 10088-3 X13MnNiN18-13-2 is commonly used for general purposes, semi-finished products, bars, rods, wire, sections and bright products. ASTM A959 XM-28 is defined under ASTM International, originating from United States, while EN 10088-3 X13MnNiN18-13-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A959 XM-28 vs EN 10088-3 X13MnNiN18-13-2 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With ASTM A959 XM-28:
IS 1570 (Part 7) 12Cr12MoH GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 ASTM A959 205 ASTM A959 .- EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 202 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 06Kh23N28 EN 10088-1 1.4006
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property ASTM A959 XM-28 EN 10088-3 X13MnNiN18-13-2
Standard ASTM A959:2011 EN 10088-3:2014
Category Stainless Steel Stainless Steel
C (%) <=0.15 <=0.15
Cr (%) 16.5-19.0 16.5-19.0
Mn (%) 11.0-14.0 11.0-14.0
N (%) 0.20-0.45 0.20-0.45
Ni (%) 0.50-2.50 0.5-2.5
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 XM-28 EN 10088-3 X13MnNiN18-13-2
Tensile Strength Not specified 690-850 MPa
Yield Strength Not specified >=380 MPa
Elongation Not specified >=30%
Hardness Not specified <=220 HB
Condition Not specified Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Typical Applications
ASTM A959 XM-28
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
EN 10088-3 X13MnNiN18-13-2
General purposes, semi-finished products, bars, rods, wire, sections and bright products
Can ASTM A959 XM-28 Be Substituted With EN 10088-3 X13MnNiN18-13-2?
ASTM A959 XM-28 and EN 10088-3 X13MnNiN18-13-2 overlap closely enough on chemistry and mechanical properties that EN 10088-3 X13MnNiN18-13-2 is often considered as a substitute for ASTM A959 XM-28 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 XM-28
0 active listings and RFQs →
EN 10088-3 X13MnNiN18-13-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 XM-28 and EN 10088-3 X13MnNiN18-13-2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 XM-28 be substituted with EN 10088-3 X13MnNiN18-13-2?
ASTM A959 XM-28 and EN 10088-3 X13MnNiN18-13-2 overlap closely enough on chemistry and mechanical properties that EN 10088-3 X13MnNiN18-13-2 is often considered as a substitute for ASTM A959 XM-28 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.