ASTM A959 XM-33 vs ASTM A240/A240M S44626

Strong Match — 94.4% match based on chemical composition and mechanical property overlap.

ASTM A959 XM-33 (ASTM A959:2011) and ASTM A240/A240M S44626 (ASTM A240/A240M:2025) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 XM-33 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A240/A240M S44626 is commonly used for pressure vessels and general applications (plate, sheet and strip). ASTM A959 XM-33 is defined under ASTM International, originating from United States, while ASTM A240/A240M S44626 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 XM-33 vs ASTM A240/A240M S44626 is a 94.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 94.4%.

Frequently Compared With ASTM A959 XM-33:
GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H ASTM A959 .- GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 06Kh23N28 EN 10088-1 1.4401
Match Breakdown
CHEMISTRY MATCH
94.4%
MECHANICAL MATCH
No shared data
OVERALL
94.4%
Specifications
Property ASTM A959 XM-33 ASTM A240/A240M S44626
Standard ASTM A959:2011 ASTM A240/A240M:2025
Category Stainless Steel Stainless Steel
C (%) <=0.06 <=0.06
Cr (%) 25.0-27.0 25.0-27.0
Cu (%) <=0.20 <=0.20
Mn (%) <=0.75 <=0.75
Mo (%) 0.75-1.50 0.75-1.50
N (%) <=0.040 <=0.04
Ni (%) <=0.50 <=0.50
P (%) <=0.040 <=0.040
S (%) <=0.020 <=0.020
Si (%) <=0.75 <=0.75
Ti (%) Not specified 0.20-1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 XM-33 ASTM A240/A240M S44626
Tensile Strength Not specified >=470 MPa
Yield Strength Not specified >=310 MPa
Elongation Not specified >=20%
Hardness Not specified <=217 HB
Condition Not specified Plate, sheet and strip; yield by 0.2 percent offset
Typical Applications
ASTM A959 XM-33
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A240/A240M S44626
Pressure vessels and general applications (plate, sheet and strip)
Key Differences
Can ASTM A959 XM-33 Be Substituted With ASTM A240/A240M S44626?
ASTM A959 XM-33 and ASTM A240/A240M S44626 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S44626 is often considered as a substitute for ASTM A959 XM-33 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 XM-33
0 active listings and RFQs →
ASTM A240/A240M S44626
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 XM-33 and ASTM A240/A240M S44626?
ASTM A240/A240M S44626 specifies Ti which is not specified for ASTM A959 XM-33.
Can ASTM A959 XM-33 be substituted with ASTM A240/A240M S44626?
ASTM A959 XM-33 and ASTM A240/A240M S44626 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S44626 is often considered as a substitute for ASTM A959 XM-33 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.