Close Alternative — 78.4% match
based on chemical composition and mechanical property overlap.
ASTM A959 XM-34 (ASTM A959:2011) and IS 11169 (Part 2) X04Cr17Mo1 (IS 11169 (Part 2):2023) are both steel grades.
Both fall under the Stainless Steel category.
ASTM A959 XM-34 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 11169 (Part 2) X04Cr17Mo1 is commonly used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 25 mm (clause 1.1, table 13).
ASTM A959 XM-34 is defined under ASTM International, originating from United States, while IS 11169 (Part 2) X04Cr17Mo1 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, ASTM A959 XM-34 vs IS 11169 (Part 2) X04Cr17Mo1 is a 78.4% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a close alternative overall at 78.4%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
ASTM A959 XM-34
IS 11169 (Part 2) X04Cr17Mo1
Reduction of Area, soft annealed (+A)
Not specified
>=60% (over 5 to 25 mm)
Tensile Strength, soft annealed (+A)
Not specified
<=600 MPa (over 5 to 25 mm)
Typical Applications
ASTM A959 XM-34
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 11169 (Part 2) X04Cr17Mo1
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 25 mm (clause 1.1, Table 13)
Can ASTM A959 XM-34 Be Substituted With IS 11169 (Part 2) X04Cr17Mo1?
ASTM A959 XM-34 and IS 11169 (Part 2) X04Cr17Mo1 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between ASTM A959 XM-34 and IS 11169 (Part 2) X04Cr17Mo1?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 XM-34 be substituted with IS 11169 (Part 2) X04Cr17Mo1?
ASTM A959 XM-34 and IS 11169 (Part 2) X04Cr17Mo1 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.