BS 4659 BH11 vs EN ISO 683-17 100Cr6

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

BS 4659 BH11 (BS 4659:1989) and EN ISO 683-17 100Cr6 (EN ISO 683-17:2014) are both steel grades. Both fall under the Tool & Die Steels category. BS 4659 BH11 is typically used for die casting dies, extrusion tooling, while EN ISO 683-17 100Cr6 is commonly used for rolling element bearings, precision components, cold work tooling. BS 4659 BH11 is defined under British Standards (BS), originating from United Kingdom, while EN ISO 683-17 100Cr6 is defined under European Standard (EN), originating from Europe.

As per chemical composition, BS 4659 BH11 vs EN ISO 683-17 100Cr6 is a 63.1% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With BS 4659 BH11:
GOST 5950 4H5MFS1 GB/T 1299 4Cr5MoSiV DIN EN ISO 4957 1.2344 GB/T 1299 4Cr5MoSiV1 GOST 5950 4H5MFS GOST 5950 3H2W8F EN ISO 4957 1.2316 DIN EN ISO 4957 1.2379 GB/T 1299 3Cr2W8V AISI 52100 IS 1570 (Part 6) 118T3 IS 1570 (Part 6) 103T3
Match Breakdown
CHEMISTRY MATCH
63.1%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property BS 4659 BH11 EN ISO 683-17 100Cr6
Standard BS 4659:1989 EN ISO 683-17:2014
Category Tool & Die Steels Tool & Die Steels
C (%) 0.33–0.43 0.93–1.05
Si (%) 0.80–1.20 0.15–0.35
Mn (%) 0.20–0.50 0.25–0.45
Cr (%) 4.75–5.50 1.35–1.65
Mo (%) 1.10–1.60 Not specified
V (%) 0.30–0.60 Not specified
S (%) Not specified ≤0.025
P (%) Not specified ≤0.025
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 4659 BH11 EN ISO 683-17 100Cr6
Hardness HRC (hardened) 40–54 Not specified
Hardness HB (annealed) ≤235 Not specified
Tensile Strength Not specified ≥620 MPa (annealed)
Hardness HRC Not specified 60–66 (hardened)
Hardness HB Not specified 179–217 (annealed)
Typical Applications
BS 4659 BH11
Die casting dies, extrusion tooling
EN ISO 683-17 100Cr6
Rolling element bearings, precision components, cold work tooling
Key Differences
Can BS 4659 BH11 Be Substituted With EN ISO 683-17 100Cr6?
BS 4659 BH11 and EN ISO 683-17 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
BS 4659 BH11
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 3500–3500 mm (137.8–137.8 in)
EN ISO 683-17 100Cr6
Round Bar → (18 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 3000–6500 mm (118.11–255.91 in)
On M-EX Right Now
BS 4659 BH11
2 active listings and RFQs →
EN ISO 683-17 100Cr6
18 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 4659 BH11 and EN ISO 683-17 100Cr6?
BS 4659 BH11 specifies Mo, V which are not specified for EN ISO 683-17 100Cr6. EN ISO 683-17 100Cr6 specifies S, P which are not specified for BS 4659 BH11.
Can BS 4659 BH11 be substituted with EN ISO 683-17 100Cr6?
BS 4659 BH11 and EN ISO 683-17 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.