BS 970 (Part 1) 080A30 vs BS 970 (Part 1) 060A32

Strong Match — 89.4% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 080A30 (BS 970 (Part 1):1983) and BS 970 (Part 1) 060A32 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Carbon Steel category. BS 970 (Part 1) 080A30 is typically used for through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of table 6., while BS 970 (Part 1) 060A32 is commonly used for through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of table 6.. BS 970 (Part 1) 080A30 is defined under British Standards (BS), originating from United Kingdom, while BS 970 (Part 1) 060A32 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, BS 970 (Part 1) 080A30 vs BS 970 (Part 1) 060A32 is a 89.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 89.4%.

Frequently Compared With BS 970 (Part 1) 080A30:
BS 970 (Part 1) 060A40 BS 970 (Part 1) 040A10 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 060A45 BS 970 (Part 1) 040A04 BS 970 (Part 1) 045M10 BS 970 (Part 1) 055M15
Match Breakdown
CHEMISTRY MATCH
89.4%
MECHANICAL MATCH
No shared data
OVERALL
89.4%
Specifications
Property BS 970 (Part 1) 080A30 BS 970 (Part 1) 060A32
Standard BS 970 (Part 1):1983 BS 970 (Part 1):1983
Category Carbon Steel Carbon Steel
C (%) 0.28-0.33 0.30-0.35
Mn (%) 0.70-0.90 0.50-0.70
P (%) <=0.050 <=0.050
S (%) <=0.050 <=0.050
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Typical Applications
BS 970 (Part 1) 080A30
Through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of Table 6.
BS 970 (Part 1) 060A32
Through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of Table 6.
Can BS 970 (Part 1) 080A30 Be Substituted With BS 970 (Part 1) 060A32?
BS 970 (Part 1) 080A30 and BS 970 (Part 1) 060A32 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 060A32 is often considered as a substitute for BS 970 (Part 1) 080A30 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 1) 080A30
0 active listings and RFQs →
BS 970 (Part 1) 060A32
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 080A30 and BS 970 (Part 1) 060A32?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can BS 970 (Part 1) 080A30 be substituted with BS 970 (Part 1) 060A32?
BS 970 (Part 1) 080A30 and BS 970 (Part 1) 060A32 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 060A32 is often considered as a substitute for BS 970 (Part 1) 080A30 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.