BS 970 (Part 1):1983 080A52: 080A52 is a carbon steel grade specified in BS 970 Part 1:1983 (Table 6, category 2). Section three of the standard advises that category 1 steels be used for new designs and established designs whenever possible.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Mn
P
S
0.50-0.55
0.70-0.90
<=0.050
<=0.050
More data from BS 970 (Part 1):1983
From the standard
Other composition limits
Phosphorus and sulphur
Each 0.050 max (clause 1.7.2.1, carbon and carbon manganese steels)
Residual elements: see clause 1.7.3.
Source: BS 970 (Part 1):1983, Table 6
Mechanical properties by heat treatment condition
Condition
Limiting ruling section (mm)
Rm (N/mm2)
Re min (N/mm2)
A min (%)
Izod min (ft lbf)
KCV min (J)
Rp0.2 min (N/mm2), when specifically ordered
HB
R
100
700-850
415
14
-
-
385
201-255
S
63
775-925
480
14
-
-
450
223-277
T (note 13)
19
850-1000
570
12
-
-
555
248-302
Values as printed in Table 6 for the limiting ruling section shown. Rp0.2 applies when specifically ordered (note 10). 1 N/mm2 = 1 MPa. Note 13: may not always be obtained by bulk heat treatment, but the properties can be achieved by the appropriate heat treatment of die forgings and components, and also apply to test bars.
Source: BS 970 (Part 1):1983, Table 6
Comparison with earlier editions
BS 970:1970/72 designation
080A52
BS 970:1955 En No.
43C
Appendix D note 47: where a comparison is made the steels are not necessarily equivalent. 'Not listed' means the earlier edition has no entry under this designation.
Source: BS 970 (Part 1):1983, Appendix D