BS 970 (Part 1) 080M15 vs IS 11169 (Part 1) 15C8

Strong Match — 95.1% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 080M15 (BS 970 (Part 1):1983) and IS 11169 (Part 1) 15C8 (IS 11169 (Part 1):1984) are both steel grades. Both fall under the Carbon Steel category. BS 970 (Part 1) 080M15 is typically used for wrought steel supplied as bright bar for mechanical and allied engineering purposes (table 4)., while IS 11169 (Part 1) 15C8 is commonly used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1). BS 970 (Part 1) 080M15 is defined under British Standards (BS), originating from United Kingdom, while IS 11169 (Part 1) 15C8 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, BS 970 (Part 1) 080M15 vs IS 11169 (Part 1) 15C8 is a 95.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 95.1%.

Frequently Compared With BS 970 (Part 1) 080M15:
BS 970 (Part 1) 080A15 BS 970 (Part 1) 080A15 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 060A32 BS 970 (Part 1) 060A40 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045A10
Match Breakdown
CHEMISTRY MATCH
95.1%
MECHANICAL MATCH
No shared data
OVERALL
95.1%
Specifications
Property BS 970 (Part 1) 080M15 IS 11169 (Part 1) 15C8
Standard BS 970 (Part 1):1983 IS 11169 (Part 1):1984
Category Carbon Steel Carbon Steel
C (%) 0.12-0.18 0.10-0.20
Mn (%) 0.60-1.00 0.60-0.90
P (%) <=0.050 Not specified
S (%) <=0.050 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 080M15 IS 11169 (Part 1) 15C8
Hardness, annealed Not specified <=140 HB
Typical Applications
BS 970 (Part 1) 080M15
Wrought steel supplied as bright bar for mechanical and allied engineering purposes (Table 4).
IS 11169 (Part 1) 15C8
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
Key Differences
Can BS 970 (Part 1) 080M15 Be Substituted With IS 11169 (Part 1) 15C8?
BS 970 (Part 1) 080M15 and IS 11169 (Part 1) 15C8 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 15C8 is often considered as a substitute for BS 970 (Part 1) 080M15 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 1) 080M15
0 active listings and RFQs →
IS 11169 (Part 1) 15C8
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 080M15 and IS 11169 (Part 1) 15C8?
BS 970 (Part 1) 080M15 specifies P, S which are not specified for IS 11169 (Part 1) 15C8.
Can BS 970 (Part 1) 080M15 be substituted with IS 11169 (Part 1) 15C8?
BS 970 (Part 1) 080M15 and IS 11169 (Part 1) 15C8 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 15C8 is often considered as a substitute for BS 970 (Part 1) 080M15 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.