BS 970 (Part 1):1983 080M30: 080M30 is a carbon steel grade specified in BS 970 Part 1:1983 (Table 6, category 1). Section three of the standard advises that category 1 steels be used for new designs and established designs whenever possible.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Mn
P
S
0.26-0.34
0.60-1.00
<=0.050
<=0.050
More data from BS 970 (Part 1):1983
From the standard
Other composition limits
Phosphorus and sulphur
Each 0.050 max (clause 1.7.2.1, carbon and carbon manganese steels)
Residual elements: see clause 1.7.3.
Source: BS 970 (Part 1):1983, Table 6
Heat treatment and maximum hardness (through hardening)
Hardening temperature
860-890 deg C
Quenching medium
Oil or water
Tempering temperature
550-660 deg C
Softened condition
Not usually supplied in the softened condition
Heat treatment to be given to test bars and to material required in the finally heat treated condition. Note 24: O = oil, W = water. Where oil hardening is specified, either a well-agitated conventional oil or a proven synthetic quenchant may be used. Synthetic quenchants shall not be used for the heat treatment of test bars for material not supplied in the finally heat treated condition.
Source: BS 970 (Part 1):1983, Table 7
Mechanical properties by heat treatment condition
Condition
Limiting ruling section (mm)
Rm (N/mm2)
Re min (N/mm2)
A min (%)
Izod min (ft lbf)
KCV min (J)
Rp0.2 min (N/mm2), when specifically ordered
HB
P
63
550-700
340
18
25
28
310
152-207
Q
19
625-775
415
16
25
28
400
179-229
Values as printed in Table 6 for the limiting ruling section shown. Rp0.2 applies when specifically ordered (note 10). 1 N/mm2 = 1 MPa.
Source: BS 970 (Part 1):1983, Table 6
Mechanical properties, bright bar
Condition
Heat treatment condition
Size, diameter or across flats (mm)
Rm (N/mm2)
Re min (N/mm2)
A min (%)
Izod min (ft lbf)
KCV min (J)
Rp0.2 min (N/mm2), when specifically ordered
HB
Normalized + turned or ground
-
6 to 150
490 min
245
20
-
-
-
143-192 (note 4)
Normalized + turned or ground
-
over 150 to 250
460 min
230
19
-
-
-
134-183 (note 4)
Hot rolled + cold drawn or hot rolled + cold drawn + ground
-
6 to 13
620 min
480
9
-
-
460
-
Hot rolled + cold drawn or hot rolled + cold drawn + ground
-
over 13 to 16
600 min
470
10
-
-
450
-
Hot rolled + cold drawn or hot rolled + cold drawn + ground
-
over 16 to 40
570 min
430
11
-
-
400
-
Hot rolled + cold drawn or hot rolled + cold drawn + ground
-
over 40 to 63
560 min
415
12
-
-
345
-
Hot rolled + cold drawn or hot rolled + cold drawn + ground
-
over 63 to 76
530 min
385
12
-
-
320
-
Hardened and tempered + turned or ground
P
6 to 63
550-700
340
18
25
28
310
152-207
Hardened and tempered + turned or ground
Q
6 to 19
625-775
415
16
25
28
400
179-229
Hardened and tempered + cold drawn or hardened and tempered + cold drawn + ground
P
6 to 63
550-700
385
13
25
-
340
152-207 (note 4)
Hardened and tempered + cold drawn or hardened and tempered + cold drawn + ground
Q
6 to 19
625-775
460
12
25
-
430
179-229 (note 4)
Size is the diameter or across flats. For cold drawn bar of 6 mm or less, all mechanical properties are subject to agreement between purchaser and supplier at the time of enquiry and order (note 8). For normalizing and hardening and tempering treatments see Tables 3 and 7 (note 9). Rp0.2 applies when specifically ordered (note 10). 1 N/mm2 = 1 MPa. Hardness values marked note 4 are for guidance only.
Appendix D note 47: where a comparison is made the steels are not necessarily equivalent. 'Not listed' means the earlier edition has no entry under this designation.
Source: BS 970 (Part 1):1983, Appendix D