BS 970 (Part 1) 214A15 vs BS 970 (Part 1) 210A15

Strong Match — 95.1% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 214A15 (BS 970 (Part 1):1983) and BS 970 (Part 1) 210A15 (BS 970 (Part 1):1991) are both steel grades. Both fall under the Free Machining Steel category. BS 970 (Part 1) 214A15 is typically used for case hardening steel for mechanical and allied engineering purposes (table 11 mechanical properties)., while BS 970 (Part 1) 210A15 is commonly used for case hardening steel (section four). BS 970 (Part 1) 214A15 is defined under British Standards (BS), originating from United Kingdom, while BS 970 (Part 1) 210A15 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, BS 970 (Part 1) 214A15 vs BS 970 (Part 1) 210A15 is a 95.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 95.1%.

Frequently Compared With BS 970 (Part 1) 214A15:
SAE J403 1117 SAE J403 1117 SAE J403 1118 SAE J403 1126 IS 4432 10C8S10 SAE J403 1126 SAE J403 1132 SAE J403 1132 IS 1570 (Part 3) 10C8S10 SAE J403 1117 SAE J403 1126 SAE J403 1118
Match Breakdown
CHEMISTRY MATCH
95.1%
MECHANICAL MATCH
No shared data
OVERALL
95.1%
Specifications
Property BS 970 (Part 1) 214A15 BS 970 (Part 1) 210A15
Standard BS 970 (Part 1):1983 BS 970 (Part 1):1991
Category Free Machining Steel Free Machining Steel
C (%) 0.13-0.18 0.13-0.18
Mn (%) 1.20-1.50 0.90-1.20
S (%) 0.10-0.18 0.10-0.18
P (%) <=0.050 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 214A15 BS 970 (Part 1) 210A15
Condition Not specified Case hardened, 19 mm test bar
Tensile Strength Not specified 460 MPa min
Elongation Not specified 16 % min
Typical Applications
BS 970 (Part 1) 214A15
Case hardening steel for mechanical and allied engineering purposes (Table 11 mechanical properties).
BS 970 (Part 1) 210A15
Case hardening steel (section four)
Key Differences
Can BS 970 (Part 1) 214A15 Be Substituted With BS 970 (Part 1) 210A15?
BS 970 (Part 1) 214A15 and BS 970 (Part 1) 210A15 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 210A15 is often considered as a substitute for BS 970 (Part 1) 214A15 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 1) 214A15
0 active listings and RFQs →
BS 970 (Part 1) 210A15
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 214A15 and BS 970 (Part 1) 210A15?
BS 970 (Part 1) 214A15 specifies P which is not specified for BS 970 (Part 1) 210A15.
Can BS 970 (Part 1) 214A15 be substituted with BS 970 (Part 1) 210A15?
BS 970 (Part 1) 214A15 and BS 970 (Part 1) 210A15 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 210A15 is often considered as a substitute for BS 970 (Part 1) 214A15 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.