BS 970 (Part 1) 216M28 vs IS 1570 (Part 3) 10C8S10

Close Alternative — 79.5% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 216M28 (BS 970 (Part 1):1983) and IS 1570 (Part 3) 10C8S10 (IS 1570 (Part 3):1979) are both steel grades. Both fall under the Free Machining Steel category. BS 970 (Part 1) 216M28 is defined under British Standards (BS), originating from United Kingdom, while IS 1570 (Part 3) 10C8S10 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, BS 970 (Part 1) 216M28 vs IS 1570 (Part 3) 10C8S10 is a 79.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 79.5%.

Frequently Compared With BS 970 (Part 1) 216M28:
SAE J403 1117 SAE J403 1118 SAE J403 1126 SAE J403 1132 SAE J403 1117 SAE J403 1118 SAE J403 1126 SAE J403 1132 IS 4432 10C8S10 SAE J403 1117 SAE J403 1118 SAE J403 1126
Match Breakdown
CHEMISTRY MATCH
79.5%
MECHANICAL MATCH
No shared data
OVERALL
79.5%
Specifications
Property BS 970 (Part 1) 216M28 IS 1570 (Part 3) 10C8S10
Standard BS 970 (Part 1):1983 IS 1570 (Part 3):1979
Category Free Machining Steel Free Machining Steel
C (%) 0.24-0.32 <=0.15
Mn (%) 1.10-1.50 0.60-0.90
Si (%) <=0.25 0.05-0.30
P (%) <=0.060 <=0.060
S (%) 0.12-0.20 0.08-0.13
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 216M28 IS 1570 (Part 3) 10C8S10
Tensile Strength Not specified 370-490 MPa
Elongation Not specified >=24%
Condition Not specified Hot rolled or normalized bars, billets and forgings (Table 2), ruling sections up to 150 mm
Typical Applications
BS 970 (Part 1) 216M28
Through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of Table 6.
IS 1570 (Part 3) 10C8S10
Not documented
Can BS 970 (Part 1) 216M28 Be Substituted With IS 1570 (Part 3) 10C8S10?
BS 970 (Part 1) 216M28 and IS 1570 (Part 3) 10C8S10 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
BS 970 (Part 1) 216M28
0 active listings and RFQs →
IS 1570 (Part 3) 10C8S10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 216M28 and IS 1570 (Part 3) 10C8S10?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can BS 970 (Part 1) 216M28 be substituted with IS 1570 (Part 3) 10C8S10?
BS 970 (Part 1) 216M28 and IS 1570 (Part 3) 10C8S10 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.