Close Alternative — 80.5% match
based on chemical composition and mechanical property overlap.
BS 970 (Part 1) 230M07 (BS 970 (Part 1):1983) and IS 4432 10C8S10 (IS 4432:1988) are both steel grades.
Both fall under the Free Machining Steel category.
BS 970 (Part 1) 230M07 is typically used for wrought steel supplied as bright bar for mechanical and allied engineering purposes (table 4)., while IS 4432 10C8S10 is commonly used for forgings and fabrication of case-hardened machine or automobile parts.
BS 970 (Part 1) 230M07 is defined under British Standards (BS), originating from United Kingdom, while IS 4432 10C8S10 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, BS 970 (Part 1) 230M07 vs IS 4432 10C8S10 is a 80.5% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a close alternative overall at 80.5%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
BS 970 (Part 1) 230M07
IS 4432 10C8S10
Core Tensile Strength
Not specified
600-850 MPa (16 mm) / 550-800 MPa (30 mm)
Core Yield Strength
Not specified
>=400 MPa (16 mm) / >=330 MPa (30 mm)
Core Elongation
Not specified
>=12% (16 mm) / >=14% (30 mm)
Core Reduction of Area
Not specified
>=35% (16 mm) / >=40% (30 mm)
Hardness, annealed (A)
Not specified
<=150 HB
Typical Applications
BS 970 (Part 1) 230M07
Wrought steel supplied as bright bar for mechanical and allied engineering purposes (Table 4).
IS 4432 10C8S10
Forgings and fabrication of case-hardened machine or automobile parts
Key Differences
IS 4432 10C8S10 specifies Si which is not specified for BS 970 (Part 1) 230M07.
Can BS 970 (Part 1) 230M07 Be Substituted With IS 4432 10C8S10?
BS 970 (Part 1) 230M07 and IS 4432 10C8S10 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between BS 970 (Part 1) 230M07 and IS 4432 10C8S10?
IS 4432 10C8S10 specifies Si which is not specified for BS 970 (Part 1) 230M07.
Can BS 970 (Part 1) 230M07 be substituted with IS 4432 10C8S10?
BS 970 (Part 1) 230M07 and IS 4432 10C8S10 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.