Strong Match — 93.8% match
based on chemical composition and mechanical property overlap.
BS 970 (Part 1) 304S11 (BS 970 (Part 1):1983) and IS 6911 X02Cr19Ni10 (IS 6911:1992) are both steel grades.
Both fall under the Stainless Steel category.
BS 970 (Part 1) 304S11 is typically used for austenitic stainless and heat resisting steel for mechanical and allied engineering purposes (table 14, with table 15 for the cold drawn condition)., while IS 6911 X02Cr19Ni10 is commonly used for stainless and heat-resisting steel plate, sheet and strip (clause 1.1).
BS 970 (Part 1) 304S11 is defined under British Standards (BS), originating from United Kingdom, while IS 6911 X02Cr19Ni10 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, BS 970 (Part 1) 304S11 vs IS 6911 X02Cr19Ni10 is a 93.8% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 93.8%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
BS 970 (Part 1) 304S11
IS 6911 X02Cr19Ni10
Bend Test (180 deg)
Not specified
Not required
Elongation (50 mm, annealed)
Not specified
>=40%
Hardness (annealed, max)
Not specified
192 HBS, 88 HRB
Tensile Strength (annealed)
Not specified
>=440 MPa
Yield Strength (0.2% proof, annealed)
Not specified
>=180 MPa
Typical Applications
BS 970 (Part 1) 304S11
Austenitic stainless and heat resisting steel for mechanical and allied engineering purposes (Table 14, with Table 15 for the cold drawn condition).
IS 6911 X02Cr19Ni10
Stainless and heat-resisting steel plate, sheet and strip (clause 1.1)
Can BS 970 (Part 1) 304S11 Be Substituted With IS 6911 X02Cr19Ni10?
BS 970 (Part 1) 304S11 and IS 6911 X02Cr19Ni10 overlap closely enough on chemistry and mechanical properties that IS 6911 X02Cr19Ni10 is often considered as a substitute for BS 970 (Part 1) 304S11 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between BS 970 (Part 1) 304S11 and IS 6911 X02Cr19Ni10?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can BS 970 (Part 1) 304S11 be substituted with IS 6911 X02Cr19Ni10?
BS 970 (Part 1) 304S11 and IS 6911 X02Cr19Ni10 overlap closely enough on chemistry and mechanical properties that IS 6911 X02Cr19Ni10 is often considered as a substitute for BS 970 (Part 1) 304S11 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.