Strong Match — 100% match
based on chemical composition and mechanical property overlap.
BS 970 (Part 1) 316S11 (BS 970 (Part 1):1983) and BS 970 (Part 3) 316S11 (BS 970 (Part 3):1991) are both steel grades.
Both fall under the Stainless Steel category.
BS 970 (Part 1) 316S11 is typically used for austenitic stainless and heat resisting steel for mechanical and allied engineering purposes (table 14, with table 15 for the cold drawn condition)., while BS 970 (Part 3) 316S11 is commonly used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; austenitic stainless and heat resisting steel (table 18).
BS 970 (Part 1) 316S11 is defined under British Standards (BS), originating from United Kingdom, while BS 970 (Part 3) 316S11 is defined under British Standards (BS), originating from United Kingdom.
As per chemical composition, BS 970 (Part 1) 316S11 vs BS 970 (Part 3) 316S11 is a 100% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 100%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Typical Applications
BS 970 (Part 1) 316S11
Austenitic stainless and heat resisting steel for mechanical and allied engineering purposes (Table 14, with Table 15 for the cold drawn condition).
BS 970 (Part 3) 316S11
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; austenitic stainless and heat resisting steel (Table 18)
Can BS 970 (Part 1) 316S11 Be Substituted With BS 970 (Part 3) 316S11?
BS 970 (Part 1) 316S11 and BS 970 (Part 3) 316S11 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 316S11 is often considered as a substitute for BS 970 (Part 1) 316S11 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between BS 970 (Part 1) 316S11 and BS 970 (Part 3) 316S11?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can BS 970 (Part 1) 316S11 be substituted with BS 970 (Part 3) 316S11?
BS 970 (Part 1) 316S11 and BS 970 (Part 3) 316S11 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 316S11 is often considered as a substitute for BS 970 (Part 1) 316S11 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.