BS 970 (Part 1) 316S31 vs EN 10088-1 1.4006

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 316S31 (BS 970 (Part 1):1983) and EN 10088-1 1.4006 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. BS 970 (Part 1) 316S31 is typically used for austenitic stainless and heat resisting steel for mechanical and allied engineering purposes (table 14, with table 15 for the cold drawn condition)., while EN 10088-1 1.4006 is commonly used for cutlery, turbine blades, fasteners, surgical instruments. BS 970 (Part 1) 316S31 is defined under British Standards (BS), originating from United Kingdom, while EN 10088-1 1.4006 is defined under European Standard (EN), originating from Europe.

As per chemical composition, BS 970 (Part 1) 316S31 vs EN 10088-1 1.4006 is a 54.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With BS 970 (Part 1) 316S31:
EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
54.6%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property BS 970 (Part 1) 316S31 EN 10088-1 1.4006
Standard BS 970 (Part 1):1983 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.07 0.08–0.15
Si (%) <=1.0 ≤1.00
Mn (%) <=2.0 ≤1.50
P (%) <=0.045 Not specified
S (%) <=0.030 Not specified
Cr (%) 16.5-18.5 11.5–13.5
Mo (%) 2.00-2.50 Not specified
Ni (%) 10.5-13.5 ≤0.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 316S31 EN 10088-1 1.4006
Tensile Strength Not specified ≥540 MPa (annealed)
Hardness HRC Not specified 36–45 (hardened)
Elongation Not specified ≥18%
Typical Applications
BS 970 (Part 1) 316S31
Austenitic stainless and heat resisting steel for mechanical and allied engineering purposes (Table 14, with Table 15 for the cold drawn condition).
EN 10088-1 1.4006
Cutlery, turbine blades, fasteners, surgical instruments
Key Differences
Can BS 970 (Part 1) 316S31 Be Substituted With EN 10088-1 1.4006?
BS 970 (Part 1) 316S31 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
BS 970 (Part 1) 316S31
No active listings currently.
EN 10088-1 1.4006
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
BS 970 (Part 1) 316S31
0 active listings and RFQs →
EN 10088-1 1.4006
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 316S31 and EN 10088-1 1.4006?
BS 970 (Part 1) 316S31 specifies P, S, Mo which are not specified for EN 10088-1 1.4006.
Can BS 970 (Part 1) 316S31 be substituted with EN 10088-1 1.4006?
BS 970 (Part 1) 316S31 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.