Strong Match — 94.4% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 403S17 (BS 970 (Part 1):1983) and ASTM A276/A276M S40500 (ASTM A276/A276M:2017) are both steel grades. Both fall under the Stainless Steel category. BS 970 (Part 1) 403S17 is typically used for stainless and heat resisting steel for mechanical and allied engineering purposes (table 13)., while ASTM A276/A276M S40500 is commonly used for stainless steel bars and shapes (hot-finished or cold-finished). BS 970 (Part 1) 403S17 is defined under British Standards (BS), originating from United Kingdom, while ASTM A276/A276M S40500 is defined under ASTM International, originating from United States.

As per chemical composition, BS 970 (Part 1) 403S17 vs ASTM A276/A276M S40500 is a 94.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 94.4%.

Frequently Compared With BS 970 (Part 1) 403S17:
GOST 5632 06Kh23N28 ASTM A959 .- EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4401
Match Breakdown
CHEMISTRY MATCH
94.4%
MECHANICAL MATCH
No shared data
OVERALL
94.4%
Specifications
Property BS 970 (Part 1) 403S17 ASTM A276/A276M S40500
Standard BS 970 (Part 1):1983 ASTM A276/A276M:2017
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Si (%) <=1.0 <=1.00
Mn (%) <=1.0 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Cr (%) 12.0-14.0 11.5-14.5
Ni (%) <=0.50 <=0.50
Al (%) Not specified 0.10-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 403S17 ASTM A276/A276M S40500
Hardness Not specified <=207 HB
Condition Not specified Condition A (Annealed), hot-finished, all sizes (first row printed)
Typical Applications
BS 970 (Part 1) 403S17
Stainless and heat resisting steel for mechanical and allied engineering purposes (Table 13).
ASTM A276/A276M S40500
Stainless steel bars and shapes (hot-finished or cold-finished)
Key Differences
Can BS 970 (Part 1) 403S17 Be Substituted With ASTM A276/A276M S40500?
BS 970 (Part 1) 403S17 and ASTM A276/A276M S40500 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S40500 is often considered as a substitute for BS 970 (Part 1) 403S17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 1) 403S17
0 active listings and RFQs →
ASTM A276/A276M S40500
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 403S17 and ASTM A276/A276M S40500?
ASTM A276/A276M S40500 specifies Al which is not specified for BS 970 (Part 1) 403S17.
Can BS 970 (Part 1) 403S17 be substituted with ASTM A276/A276M S40500?
BS 970 (Part 1) 403S17 and ASTM A276/A276M S40500 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S40500 is often considered as a substitute for BS 970 (Part 1) 403S17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.