BS 970 (Part 1) 410S21 vs IS 11169 (Part 2) X12Cr13

Strong Match — 94.9% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 410S21 (BS 970 (Part 1):1983) and IS 11169 (Part 2) X12Cr13 (IS 11169 (Part 2):2023) are both steel grades. Both fall under the Stainless Steel category. BS 970 (Part 1) 410S21 is typically used for stainless and heat resisting steel for mechanical and allied engineering purposes (table 13)., while IS 11169 (Part 2) X12Cr13 is commonly used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 100 mm (clause 1.1, table 14). BS 970 (Part 1) 410S21 is defined under British Standards (BS), originating from United Kingdom, while IS 11169 (Part 2) X12Cr13 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, BS 970 (Part 1) 410S21 vs IS 11169 (Part 2) X12Cr13 is a 94.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 94.9%.

Frequently Compared With BS 970 (Part 1) 410S21:
IS 1570 (Part 7) 12Cr13H EN 10088-1 1.4845 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH EN 10088-1 1.4006 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
94.9%
MECHANICAL MATCH
No shared data
OVERALL
94.9%
Specifications
Property BS 970 (Part 1) 410S21 IS 11169 (Part 2) X12Cr13
Standard BS 970 (Part 1):1983 IS 11169 (Part 2):2023
Category Stainless Steel Stainless Steel
C (%) 0.09-0.15 0.08-0.15
Si (%) <=1.0 <=1.00
Mn (%) <=1.0 <=1.50
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Cr (%) 11.5-13.5 11.5-13.5
Ni (%) <=1.00 <=0.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 410S21 IS 11169 (Part 2) X12Cr13
Reduction of Area, soft annealed (+A) Not specified >=60% (over 5 to 100 mm)
Tensile Strength, soft annealed (+A) Not specified <=600 MPa (over 5 to 100 mm)
Typical Applications
BS 970 (Part 1) 410S21
Stainless and heat resisting steel for mechanical and allied engineering purposes (Table 13).
IS 11169 (Part 2) X12Cr13
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 100 mm (clause 1.1, Table 14)
Can BS 970 (Part 1) 410S21 Be Substituted With IS 11169 (Part 2) X12Cr13?
BS 970 (Part 1) 410S21 and IS 11169 (Part 2) X12Cr13 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X12Cr13 is often considered as a substitute for BS 970 (Part 1) 410S21 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 1) 410S21
0 active listings and RFQs →
IS 11169 (Part 2) X12Cr13
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 410S21 and IS 11169 (Part 2) X12Cr13?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can BS 970 (Part 1) 410S21 be substituted with IS 11169 (Part 2) X12Cr13?
BS 970 (Part 1) 410S21 and IS 11169 (Part 2) X12Cr13 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X12Cr13 is often considered as a substitute for BS 970 (Part 1) 410S21 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.