BS 970 (Part 1) 416S29 vs BS 970 (Part 3) 416S41

Strong Match — 89.6% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 416S29 (BS 970 (Part 1):1983) and BS 970 (Part 3) 416S41 (BS 970 (Part 3):1991) are both steel grades. Both fall under the Stainless Steel category. BS 970 (Part 1) 416S29 is typically used for stainless and heat resisting steel for mechanical and allied engineering purposes (table 13)., while BS 970 (Part 3) 416S41 is commonly used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; martensitic stainless steel (table 17). BS 970 (Part 1) 416S29 is defined under British Standards (BS), originating from United Kingdom, while BS 970 (Part 3) 416S41 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, BS 970 (Part 1) 416S29 vs BS 970 (Part 3) 416S41 is a 89.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 89.6%.

Frequently Compared With BS 970 (Part 1) 416S29:
IS 1570 (Part 7) 12Cr13H EN 10088-1 1.4845 ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
89.6%
MECHANICAL MATCH
No shared data
OVERALL
89.6%
Specifications
Property BS 970 (Part 1) 416S29 BS 970 (Part 3) 416S41
Standard BS 970 (Part 1):1983 BS 970 (Part 3):1991
Category Stainless Steel Stainless Steel
C (%) 0.14-0.20 0.09-0.15
Si (%) <=1.0 <=1.0
Mn (%) <=1.5 <=1.5
P (%) <=0.060 <=0.060
S (%) 0.15-0.35 <=0.060
Cr (%) 11.5-13.5 11.5-13.5
Mo (%) <=0.60 <=0.60
Ni (%) <=1.00 <=1.00
Se (%) Not specified 0.15-0.35
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Typical Applications
BS 970 (Part 1) 416S29
Stainless and heat resisting steel for mechanical and allied engineering purposes (Table 13).
BS 970 (Part 3) 416S41
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; martensitic stainless steel (Table 17)
Key Differences
Can BS 970 (Part 1) 416S29 Be Substituted With BS 970 (Part 3) 416S41?
BS 970 (Part 1) 416S29 and BS 970 (Part 3) 416S41 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 416S41 is often considered as a substitute for BS 970 (Part 1) 416S29 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 1) 416S29
0 active listings and RFQs →
BS 970 (Part 3) 416S41
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 416S29 and BS 970 (Part 3) 416S41?
BS 970 (Part 3) 416S41 specifies Se which is not specified for BS 970 (Part 1) 416S29.
Can BS 970 (Part 1) 416S29 be substituted with BS 970 (Part 3) 416S41?
BS 970 (Part 1) 416S29 and BS 970 (Part 3) 416S41 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 416S41 is often considered as a substitute for BS 970 (Part 1) 416S29 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.