BS 970 (Part 1):1983 527A17: 527A17 is a case hardening alloy steel grade specified in BS 970 Part 1:1983 (Table 11, category 2). Section three of the standard advises that category 1 steels be used for new designs and established designs whenever possible.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Mn
Cr
P
S
0.14-0.19
0.70-0.90
0.70-0.90
<=0.035
<=0.040
More data from BS 970 (Part 1):1983
From the standard
Other composition limits
Phosphorus and sulphur
P 0.035 max, S 0.040 max, alloy steels (clause 1.7.2.1)
Residual elements: see clause 1.7.3.
Source: BS 970 (Part 1):1983, clause 1.7.2.1
Mechanical properties, test bar
Test bar diameter (mm)
Rm min (N/mm2)
A min (%)
Izod min (ft lbf)
KCV min (J)
19
770
12
15 (note 29)
16 (note 29)
Values as printed in Table 11 for the test bar diameter shown. 1 N/mm2 = 1 MPa. Note 29: these are new steels which may have been conservatively rated due to limited data.
Source: BS 970 (Part 1):1983, Table 11
Comparison with earlier editions
BS 970:1970/72 designation
Not listed
BS 970:1955 En No.
None
Appendix D note 47: where a comparison is made the steels are not necessarily equivalent. 'Not listed' means the earlier edition has no entry under this designation.
Source: BS 970 (Part 1):1983, Appendix D