BS 970 (Part 1) 527M17 vs NF A35-565 100C6

Related Material — 69.7% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 527M17 (BS 970 (Part 1):1983) and NF A35-565 100C6 are both steel grades. Both fall under the Alloy Steel category. BS 970 (Part 1) 527M17 is typically used for case hardening steel for mechanical and allied engineering purposes (table 11 mechanical properties)., while NF A35-565 100C6 is commonly used for ball bearings, roller bearings, bearing races, rollers, precision tools, wear resistant parts. BS 970 (Part 1) 527M17 is defined under British Standards (BS), originating from United Kingdom, while NF A35-565 100C6 is defined under Association Francaise de Normalisation (NF), originating from France.

As per chemical composition, BS 970 (Part 1) 527M17 vs NF A35-565 100C6 is a 69.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.7%.

Frequently Compared With BS 970 (Part 1) 527M17:
IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 07Cr4Mo6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H IS 11169 (Part 1) 10Ni5Cr4 UNI 11234 100Cr6 IS 1570 (Part 4) 105Cr5
Match Breakdown
CHEMISTRY MATCH
69.7%
MECHANICAL MATCH
No shared data
OVERALL
69.7%
Specifications
Property BS 970 (Part 1) 527M17 NF A35-565 100C6
Standard BS 970 (Part 1):1983 NF A35-565
Category Alloy Steel Alloy Steel
C (%) 0.14-0.20 0.95-1.05
Mn (%) 0.70-1.00 0.25-0.45
Cr (%) 0.60-0.90 1.35-1.65
P (%) <=0.035 <=0.027
S (%) <=0.040 <=0.025
Si (%) Not specified 0.15-0.35
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 527M17 NF A35-565 100C6
Tensile Strength Not specified 850-1100 MPa
Hardness Not specified 60-66 HRC
Typical Applications
BS 970 (Part 1) 527M17
Case hardening steel for mechanical and allied engineering purposes (Table 11 mechanical properties).
NF A35-565 100C6
ball bearings, roller bearings, bearing races, rollers, precision tools, wear resistant parts
Key Differences
Can BS 970 (Part 1) 527M17 Be Substituted With NF A35-565 100C6?
BS 970 (Part 1) 527M17 and NF A35-565 100C6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
BS 970 (Part 1) 527M17
No active listings currently.
NF A35-565 100C6
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 6700–6700 mm (263.78–263.78 in)
On M-EX Right Now
BS 970 (Part 1) 527M17
0 active listings and RFQs →
NF A35-565 100C6
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 527M17 and NF A35-565 100C6?
NF A35-565 100C6 specifies Si which is not specified for BS 970 (Part 1) 527M17.
Can BS 970 (Part 1) 527M17 be substituted with NF A35-565 100C6?
BS 970 (Part 1) 527M17 and NF A35-565 100C6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.