BS 970 (Part 1) 590M17 vs IS 11169 (Part 1) 16Mn5Cr4

Strong Match — 91.4% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 590M17 (BS 970 (Part 1):1983) and IS 11169 (Part 1) 16Mn5Cr4 (IS 11169 (Part 1):1984) are both steel grades. Both fall under the Alloy Steel category. BS 970 (Part 1) 590M17 is typically used for case hardening steel for mechanical and allied engineering purposes (table 11 mechanical properties)., while IS 11169 (Part 1) 16Mn5Cr4 is commonly used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1). BS 970 (Part 1) 590M17 is defined under British Standards (BS), originating from United Kingdom, while IS 11169 (Part 1) 16Mn5Cr4 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, BS 970 (Part 1) 590M17 vs IS 11169 (Part 1) 16Mn5Cr4 is a 91.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 91.4%.

Frequently Compared With BS 970 (Part 1) 590M17:
IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 IS 4367 07Cr4Mo6 NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Mo6H IS 11169 (Part 1) 10Ni5Cr4
Match Breakdown
CHEMISTRY MATCH
91.4%
MECHANICAL MATCH
No shared data
OVERALL
91.4%
Specifications
Property BS 970 (Part 1) 590M17 IS 11169 (Part 1) 16Mn5Cr4
Standard BS 970 (Part 1):1983 IS 11169 (Part 1):1984
Category Alloy Steel Alloy Steel
C (%) 0.14-0.20 0.14-0.19
Mn (%) 1.00-1.30 1.00-1.30
Cr (%) 0.80-1.10 0.80-1.10
P (%) <=0.035 Not specified
S (%) <=0.040 Not specified
Si (%) Not specified 0.10-0.35
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 590M17 IS 11169 (Part 1) 16Mn5Cr4
Core Tensile Strength Not specified >=800 MPa (30 mm)
Core Elongation Not specified >=10% (30 mm)
Hardness, annealed Not specified <=160 HB
Typical Applications
BS 970 (Part 1) 590M17
Case hardening steel for mechanical and allied engineering purposes (Table 11 mechanical properties).
IS 11169 (Part 1) 16Mn5Cr4
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
Key Differences
Can BS 970 (Part 1) 590M17 Be Substituted With IS 11169 (Part 1) 16Mn5Cr4?
BS 970 (Part 1) 590M17 and IS 11169 (Part 1) 16Mn5Cr4 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 16Mn5Cr4 is often considered as a substitute for BS 970 (Part 1) 590M17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 1) 590M17
0 active listings and RFQs →
IS 11169 (Part 1) 16Mn5Cr4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 590M17 and IS 11169 (Part 1) 16Mn5Cr4?
BS 970 (Part 1) 590M17 specifies P, S which are not specified for IS 11169 (Part 1) 16Mn5Cr4. IS 11169 (Part 1) 16Mn5Cr4 specifies Si which is not specified for BS 970 (Part 1) 590M17.
Can BS 970 (Part 1) 590M17 be substituted with IS 11169 (Part 1) 16Mn5Cr4?
BS 970 (Part 1) 590M17 and IS 11169 (Part 1) 16Mn5Cr4 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 16Mn5Cr4 is often considered as a substitute for BS 970 (Part 1) 590M17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.