BS 970 (Part 1) 605A32 vs IS 4367 35Mn6Mo3

Strong Match — 85.6% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 605A32 (BS 970 (Part 1):1983) and IS 4367 35Mn6Mo3 (IS 4367:1991) are both steel grades. Both fall under the Alloy Steel category. BS 970 (Part 1) 605A32 is defined under British Standards (BS), originating from United Kingdom, while IS 4367 35Mn6Mo3 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, BS 970 (Part 1) 605A32 vs IS 4367 35Mn6Mo3 is a 85.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 85.6%.

Frequently Compared With BS 970 (Part 1) 605A32:
IS 4367 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 7) 10Mo6H IS 1570 (Part 4) 07Cr4Mo6 NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6
Match Breakdown
CHEMISTRY MATCH
85.6%
MECHANICAL MATCH
No shared data
OVERALL
85.6%
Specifications
Property BS 970 (Part 1) 605A32 IS 4367 35Mn6Mo3
Standard BS 970 (Part 1):1983 IS 4367:1991
Category Alloy Steel Alloy Steel
C (%) 0.30-0.35 0.30-0.40
Mn (%) 1.30-1.70 1.30-1.80
Mo (%) 0.22-0.32 0.20-0.35
P (%) <=0.035 <=0.035
S (%) <=0.040 <=0.035
Si (%) Not specified 0.10-0.35
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 605A32 IS 4367 35Mn6Mo3
Tensile Strength Not specified 700-850 MPa
Yield Strength Not specified 540 MPa min
Elongation Not specified >=18%
Izod Impact Not specified 55 J min
Hardness Not specified 208-252 HB
Hardness (soft annealed) Not specified <=220 HB
Condition Not specified Hardened and tempered, ruling section up to 150 mm
Typical Applications
BS 970 (Part 1) 605A32
Through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of Table 6.
IS 4367 35Mn6Mo3
Not documented
Key Differences
Can BS 970 (Part 1) 605A32 Be Substituted With IS 4367 35Mn6Mo3?
BS 970 (Part 1) 605A32 and IS 4367 35Mn6Mo3 overlap closely enough on chemistry and mechanical properties that IS 4367 35Mn6Mo3 is often considered as a substitute for BS 970 (Part 1) 605A32 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 1) 605A32
0 active listings and RFQs →
IS 4367 35Mn6Mo3
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 605A32 and IS 4367 35Mn6Mo3?
IS 4367 35Mn6Mo3 specifies Si which is not specified for BS 970 (Part 1) 605A32.
Can BS 970 (Part 1) 605A32 be substituted with IS 4367 35Mn6Mo3?
BS 970 (Part 1) 605A32 and IS 4367 35Mn6Mo3 overlap closely enough on chemistry and mechanical properties that IS 4367 35Mn6Mo3 is often considered as a substitute for BS 970 (Part 1) 605A32 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.