BS 970 (Part 1) 708A47 vs IS 11169 (Part 1) 10Ni5Cr4

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 708A47 (BS 970 (Part 1):1983) and IS 11169 (Part 1) 10Ni5Cr4 (IS 11169 (Part 1):2022) are both steel grades. Both fall under the Alloy Steel category. BS 970 (Part 1) 708A47 is typically used for through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of table 6., while IS 11169 (Part 1) 10Ni5Cr4 is commonly used for cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex b). BS 970 (Part 1) 708A47 is defined under British Standards (BS), originating from United Kingdom, while IS 11169 (Part 1) 10Ni5Cr4 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, BS 970 (Part 1) 708A47 vs IS 11169 (Part 1) 10Ni5Cr4 is a 61.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With BS 970 (Part 1) 708A47:
IS 1570 (Part 4) 103Cr6 NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 IS 4367 10Cr9Mo10 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 UNI 11234 100Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 7) 10Mo6H IS 1570 (Part 4) 10Mo6
Match Breakdown
CHEMISTRY MATCH
61.8%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property BS 970 (Part 1) 708A47 IS 11169 (Part 1) 10Ni5Cr4
Standard BS 970 (Part 1):1983 IS 11169 (Part 1):2022
Category Alloy Steel Alloy Steel
C (%) 0.45-0.50 0.07-0.12
Mn (%) 0.75-1.00 0.60-0.90
Cr (%) 0.90-1.20 0.90-1.20
Mo (%) 0.15-0.25 Not specified
P (%) <=0.035 <=0.025
S (%) <=0.040 <=0.025
Cu (%) Not specified <=0.25
Ni (%) Not specified 1.20-1.50
Si (%) Not specified <=0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 708A47 IS 11169 (Part 1) 10Ni5Cr4
Hardness, ferrite-pearlite (+FP) Not specified 137-187 HB
Tensile Strength, annealed (+AC) Not specified <=520 MPa (over 5 to 40 mm)
Typical Applications
BS 970 (Part 1) 708A47
Through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of Table 6.
IS 11169 (Part 1) 10Ni5Cr4
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
Key Differences
Can BS 970 (Part 1) 708A47 Be Substituted With IS 11169 (Part 1) 10Ni5Cr4?
BS 970 (Part 1) 708A47 and IS 11169 (Part 1) 10Ni5Cr4 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
BS 970 (Part 1) 708A47
0 active listings and RFQs →
IS 11169 (Part 1) 10Ni5Cr4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 708A47 and IS 11169 (Part 1) 10Ni5Cr4?
BS 970 (Part 1) 708A47 specifies Mo which is not specified for IS 11169 (Part 1) 10Ni5Cr4. IS 11169 (Part 1) 10Ni5Cr4 specifies Cu, Ni, Si which are not specified for BS 970 (Part 1) 708A47.
Can BS 970 (Part 1) 708A47 be substituted with IS 11169 (Part 1) 10Ni5Cr4?
BS 970 (Part 1) 708A47 and IS 11169 (Part 1) 10Ni5Cr4 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.