BS 970 (Part 1) 805A20 vs IS 4432 20Ni2Cr2Mo2

Strong Match — 93.9% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 805A20 (BS 970 (Part 1):1983) and IS 4432 20Ni2Cr2Mo2 (IS 4432:1988) are both steel grades. Both fall under the Alloy Steel category. BS 970 (Part 1) 805A20 is typically used for case hardening steel for mechanical and allied engineering purposes (table 11 mechanical properties)., while IS 4432 20Ni2Cr2Mo2 is commonly used for forgings and fabrication of case-hardened machine or automobile parts. BS 970 (Part 1) 805A20 is defined under British Standards (BS), originating from United Kingdom, while IS 4432 20Ni2Cr2Mo2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, BS 970 (Part 1) 805A20 vs IS 4432 20Ni2Cr2Mo2 is a 93.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 93.9%.

Frequently Compared With BS 970 (Part 1) 805A20:
IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 NF A35-565 100C6 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 UNI 11234 100Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 7) 10Mo6H IS 11169 (Part 1) 10Ni5Cr4
Match Breakdown
CHEMISTRY MATCH
93.9%
MECHANICAL MATCH
No shared data
OVERALL
93.9%
Specifications
Property BS 970 (Part 1) 805A20 IS 4432 20Ni2Cr2Mo2
Standard BS 970 (Part 1):1983 IS 4432:1988
Category Alloy Steel Alloy Steel
C (%) 0.18-0.23 0.18-0.23
Mn (%) 0.70-0.90 0.70-0.90
Cr (%) 0.40-0.60 0.40-0.60
Mo (%) 0.15-0.25 0.15-0.25
Ni (%) 0.40-0.70 0.40-0.70
P (%) <=0.035 <=0.035
S (%) <=0.040 <=0.035
Si (%) Not specified 0.15-0.35
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 805A20 IS 4432 20Ni2Cr2Mo2
Core Tensile Strength Not specified 850-1200 MPa (16 mm) / 800-1150 MPa (30 mm) / 750-1050 MPa (63 mm)
Core Yield Strength Not specified >=600 MPa (16 mm) / >=550 MPa (30 mm) / >=520 MPa (63 mm)
Core Elongation Not specified >=8% (16 mm) / >=9% (30 mm) / >=10% (63 mm)
Core Reduction of Area Not specified >=35% (16 mm) / >=35% (30 mm) / >=40% (63 mm)
Hardness, annealed (A) Not specified <=217 HB
Typical Applications
BS 970 (Part 1) 805A20
Case hardening steel for mechanical and allied engineering purposes (Table 11 mechanical properties).
IS 4432 20Ni2Cr2Mo2
Forgings and fabrication of case-hardened machine or automobile parts
Key Differences
Can BS 970 (Part 1) 805A20 Be Substituted With IS 4432 20Ni2Cr2Mo2?
BS 970 (Part 1) 805A20 and IS 4432 20Ni2Cr2Mo2 overlap closely enough on chemistry and mechanical properties that IS 4432 20Ni2Cr2Mo2 is often considered as a substitute for BS 970 (Part 1) 805A20 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 1) 805A20
0 active listings and RFQs →
IS 4432 20Ni2Cr2Mo2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 805A20 and IS 4432 20Ni2Cr2Mo2?
IS 4432 20Ni2Cr2Mo2 specifies Si which is not specified for BS 970 (Part 1) 805A20.
Can BS 970 (Part 1) 805A20 be substituted with IS 4432 20Ni2Cr2Mo2?
BS 970 (Part 1) 805A20 and IS 4432 20Ni2Cr2Mo2 overlap closely enough on chemistry and mechanical properties that IS 4432 20Ni2Cr2Mo2 is often considered as a substitute for BS 970 (Part 1) 805A20 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.