BS 970 (Part 1) 805A22 vs BS 970 (Part 1) 805A17

Strong Match — 91.1% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 805A22 (BS 970 (Part 1):1983) and BS 970 (Part 1) 805A17 (BS 970 (Part 1):1991) are both steel grades. Both fall under the Alloy Steel category. BS 970 (Part 1) 805A22 is typically used for case hardening steel for mechanical and allied engineering purposes (table 11 mechanical properties)., while BS 970 (Part 1) 805A17 is commonly used for case hardening steel (section four). BS 970 (Part 1) 805A22 is defined under British Standards (BS), originating from United Kingdom, while BS 970 (Part 1) 805A17 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, BS 970 (Part 1) 805A22 vs BS 970 (Part 1) 805A17 is a 91.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 91.1%.

Frequently Compared With BS 970 (Part 1) 805A22:
IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 11169 (Part 1) 10Ni5Cr4 NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6
Match Breakdown
CHEMISTRY MATCH
91.1%
MECHANICAL MATCH
No shared data
OVERALL
91.1%
Specifications
Property BS 970 (Part 1) 805A22 BS 970 (Part 1) 805A17
Standard BS 970 (Part 1):1983 BS 970 (Part 1):1991
Category Alloy Steel Alloy Steel
C (%) 0.20-0.25 0.15-0.20
Mn (%) 0.70-0.90 0.70-0.90
Cr (%) 0.40-0.60 0.40-0.60
Mo (%) 0.15-0.25 0.15-0.25
Ni (%) 0.40-0.70 0.40-0.70
P (%) <=0.035 <=0.035
S (%) <=0.040 <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 805A22 BS 970 (Part 1) 805A17
Condition Not specified Case hardened, 19 mm test bar
Tensile Strength Not specified 770 MPa min
Elongation Not specified 12 % min
Typical Applications
BS 970 (Part 1) 805A22
Case hardening steel for mechanical and allied engineering purposes (Table 11 mechanical properties).
BS 970 (Part 1) 805A17
Case hardening steel (section four)
Can BS 970 (Part 1) 805A22 Be Substituted With BS 970 (Part 1) 805A17?
BS 970 (Part 1) 805A22 and BS 970 (Part 1) 805A17 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 805A17 is often considered as a substitute for BS 970 (Part 1) 805A22 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 1) 805A22
0 active listings and RFQs →
BS 970 (Part 1) 805A17
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 805A22 and BS 970 (Part 1) 805A17?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can BS 970 (Part 1) 805A22 be substituted with BS 970 (Part 1) 805A17?
BS 970 (Part 1) 805A22 and BS 970 (Part 1) 805A17 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 805A17 is often considered as a substitute for BS 970 (Part 1) 805A22 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.