BS 970 (Part 1) 808H17 vs BS 970 (Part 1) 808M17

Strong Match — 98.6% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 808H17 (BS 970 (Part 1):1983) and BS 970 (Part 1) 808M17 (BS 970 (Part 1):1991) are both steel grades. Both fall under the Alloy Steel category. BS 970 (Part 1) 808H17 is typically used for case hardening steel supplied to specified hardenability limits (end quench test, table 10)., while BS 970 (Part 1) 808M17 is commonly used for case hardening steel (section four). BS 970 (Part 1) 808H17 is defined under British Standards (BS), originating from United Kingdom, while BS 970 (Part 1) 808M17 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, BS 970 (Part 1) 808H17 vs BS 970 (Part 1) 808M17 is a 98.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 98.6%.

Frequently Compared With BS 970 (Part 1) 808H17:
IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 UNI 11234 100Cr6 IS 11169 (Part 1) 10Ni5Cr4 IS 1570 (Part 4) 07Cr4Mo6 NF A35-565 100C6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H IS 1570 (Part 4) 105Cr5
Match Breakdown
CHEMISTRY MATCH
98.6%
MECHANICAL MATCH
No shared data
OVERALL
98.6%
Specifications
Property BS 970 (Part 1) 808H17 BS 970 (Part 1) 808M17
Standard BS 970 (Part 1):1983 BS 970 (Part 1):1991
Category Alloy Steel Alloy Steel
C (%) 0.14-0.20 0.14-0.20
Mn (%) 0.70-1.05 0.70-1.05
Cr (%) 0.35-0.65 0.35-0.65
Mo (%) 0.30-0.40 0.30-0.40
Ni (%) 0.35-0.75 0.35-0.75
P (%) <=0.035 Not specified
S (%) <=0.040 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 808H17 BS 970 (Part 1) 808M17
Condition Not specified Case hardened, 19 mm test bar
Tensile Strength Not specified 930 MPa min
Elongation Not specified 10 % min
Typical Applications
BS 970 (Part 1) 808H17
Case hardening steel supplied to specified hardenability limits (end quench test, Table 10).
BS 970 (Part 1) 808M17
Case hardening steel (section four)
Key Differences
Can BS 970 (Part 1) 808H17 Be Substituted With BS 970 (Part 1) 808M17?
BS 970 (Part 1) 808H17 and BS 970 (Part 1) 808M17 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 808M17 is often considered as a substitute for BS 970 (Part 1) 808H17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 1) 808H17
0 active listings and RFQs →
BS 970 (Part 1) 808M17
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 808H17 and BS 970 (Part 1) 808M17?
BS 970 (Part 1) 808H17 specifies P, S which are not specified for BS 970 (Part 1) 808M17.
Can BS 970 (Part 1) 808H17 be substituted with BS 970 (Part 1) 808M17?
BS 970 (Part 1) 808H17 and BS 970 (Part 1) 808M17 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 808M17 is often considered as a substitute for BS 970 (Part 1) 808H17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.